Abstract:The interface structure and infiltration effect between reinforcement (CFs) and Al matrix have a significant impact upon comprehensive properties of the resulting carbon-fibre-reinforced Al matrix (CF/Al) composites. In present study, Ni coatings with different thicknesses were evenly coated onto carbon fibres (CFs) via electroplating for the purpose of promote the interface combining effect and reduce adverse interfacial reaction betwixt CFs and Al matrix. The influence of pH value (2, 3, 4, 5, 6), current density (0.1 A, 0.2 A, 0.3 A, 0.4 A, 0.5 A, 0.6 A), electroplating time (2 min, 4 min, 6 min) on surface appearance and tensile strength of Ni-coated CFs were discussed. The results show that the Ni-coated CFs with excellent integrity and mechanical properties was obtained at a current density of 0.4 A and a pH of 5. Subsequently, twin-roll casting and T6 heat treatment process were used to fabricate CF/Al composites with varying Ni coating thicknesses. Using SEM, TEM and tensile property testing, the impact of Ni coating thickness (0 μm, 0.35 μm, 0.58 μm, 0.76 μm) on interfacial microstructures and mechanical characteristics of CF/Al composites were examined. The results exhibit that the 0.76 μm Ni-coated CF/Al composites exhibit best UTS and elongation of 151.6 MPa and 11.7 %, respectively. This is due to a thicker Ni coating preventing the CFs against reaction with Al matrix during processing the composites, which reduces the generation of Al 4 C 3 phase. However, when the coating thickness is 0.35 μm, adverse chemical interactions occur at interface of Al-CFs, leading to the formation of an Al 4 C 3 phase. Finally, the strengthening mechanism of Ni-coated CF/Al composites was analyzed, and its strengthening model was established. This study can provide a pratical route to prepare and applicate the high-quality continuous CF/Al composites.

Ni Plating on Carbon Fiber on the Condition of Alkali

A Study on the Surface Oxidation Pretreatment and Nickel Plating Mechanism of Carbon Fiber

Preliminary Study on Electroless Nickel Plating for Surface Modification of Carbon Fiber

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

Study on new process of electroless copper plating pretreatment on carbon fiber surface

Preparation of Hollow Nickel Fibres by Electroless-Plating Technique

CHEMICAL PLATING MECHANISM IN ACID BATHS AND FABRICATION OF Ni-P COATING WITH HIGH P CONTENT

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Preparation and Characterization of Nano-Particles Nickel Hollow Fibers

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

A Method for Electroless Nickel Plating on Aluminum Alloy Surface

Preparation and characterisation of the Ni-C composite coating electrodeposited with carbon sol

Electrochemical study of Ni deposition on carbon microfiber

Preparation for the Hollow Nickel Fibres of the Positive Current Collector by Electroless Plating Technique

ELECTROLESS PLATED MULTIWALLED CARBON NANOTUBES FOR REINFORCING METAL-MATRIX COMPOSITES

Effect of surface modification on interfacial microstructures and mechanical properties of continuous CF/Al composites

Effect of nickel electroplating followed by a further copper electroplating on the micro-structure and mechanical properties of high modulus carbon fibers

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Study on Electroless Cobalt Plating Technology on Carbon Fiber