Abstract:Experimental study of the anodic dissolution of titanium and its alloys over a wide range of current densities, including pulsed currents (up to 100 A/cm 2 ), under controlled hydrodynamic conditions and surface temperature in nitrate and chloride solutions, showed that the process is mediated by electrochemical formation of an anodic oxide film (AOF), which undergoes chemical dissolution. The AOF has a bilayer structure (two barrier films: at the interface with the metal and solution). It is described by PDM-III (Point Defect Model). Under certain conditions, it is possible to achieve a steady state in which the film growth rate is compensated by the rate of its chemical dissolution (during a pulsed treatment). In this case, there is a 100% current efficiency in terms of titanium ionization in the oxidation state of four. Under the conditions of the described experiments, i.e., when using direct current, the rate of the AOF electrochemical formation exceeds that of its chemical dissolution, which leads to a decrease in the current efficiency, which does not exceed 75%. Due to the temperature dependence of the electrical resistance of the barrier film at the interface with the solution, which determines its thickness, the current efficiency increases with an increase in the flow rate of the electrolyte. When the thermokinetic instability (TKI) of the AOF is reached (thermal explosion caused by positive feedback: the rate of electrochemical reaction–surface temperature–the rate of electrochemical reaction), the interaction of electrolyte components with the surface free from the film leads to "anomalous" anodic dissolution of the AOF with a current efficiency exceeding 100%. Regardless of the nature of the electrolyte, the TKI conditions are reached at ~1 A/cm 2 . It has been shown that the dissolution rate in nitrate solutions for certain pulsed treatment parameters (relative pulse duration of 2, dc = 50%) (and the displacement of cathode tool in electrochemical machining) may exceed the machining rate with direct current of the same density by more than a factor of two.

Influence of Pulse Parameters on Electrodeposition of Titanium from NaCl-KCl-TiCl2 Melt

Electrodeposition of titanium from chloride melts

Equilibrium between titanium ions and high-purity titanium electrorefining in a NaCl-KCl melt

Investigation on the reaction progress of titanium and lead chloride in NaCl-KCl melt

Electrodeposition of Titanium from an Ionic Liquid

Electrode processes in the production of microdispersed titanium powder by volumetric electrolytic reduction of its ions with sodium dissolved in the BaCl2–CaCl2–NaCl melt in the absence of titanium halides in the initial melt

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Anodic behavior in AlCl3-EMIC ionic liquid of Ti6Al4V alloy and its application for enhancing the adhesion strength of aluminum coatings

The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Electrosynthesis of Titanium from High-Titanium Slag with Short-Process in Molten CaCl2

Electrochemical Polishing Method for Titanium Alloys with a Microgroove Structure

Influence of Target Current on Microstructures and Stoichiometries of TiAlN Coating Deposited by Arc Ion Plating

Dynamic evolution of high-temperature molten salt electrolysis of titanium under different operational conditions

Electrochemical extraction of titanium from carbon-doped titanium dioxide precursors by electrolysis in chloride molten salt

Influence of Process Parameters on The Electrodeposition of Vanadium in NaCl-KCl-NaF-V2O3 Molten Salt

Effect of Passive Oxide Film Structure and Surface Temperature on the Rate of Anodic Dissolution of Chromium-Nickel and Titanium Alloys in Electrolytes for Electrochemical Machining: Part 2. Anodic Dissolution of Titanium Alloys in Nitrate and Chloride Solutions

Improving Surface Properties of Titanium Alloys by Electrospark Deposition with Low Pulse Energy

Synthesis of Ti powders with different morphologies via controlling the valence state of the titanium ion in KCl-NaCl molten salt

Electrochemical Micromachining on Titanium Using the NaCl-containing Ethylene Glycol Electrolyte

Effect of electropulsing intensity on nucleation of TiN in 321 stainless steel

Investigation of the Electrochemical Reduction of Porous CaTiO 3 Pellets in CaCl 2 -0.5%CaO Molten Salt