Abstract:ZrC precursor was synthesized by a solution approach using ZrOCl2·8H2O, acetylacetonate, glycerol and boron-modified phenolic resin. A ZrC yield of ~ 40.56wt% was obtained at 1500°C in the C/Zr molar ratio of 1:1. C/C-ZrC-SiC composites were fabricated by a combined processes of chemical vapor infiltration (CVI) and precursor infiltration and pyrolysis (PIP) using the synthesized ZrC precursor. For comparison, C/C-SiC composites were prepared by CVI. Thermogravimetric analysis showed that C/C-ZrC-SiC composites exhibited better oxidation resistance than C/C-SiC composites. After oxyacetylene torch ablation, the mass ablation rate of C/C-ZrC-SiC composites was 9.23% lower than that of C/C-SiC composites. The porous ZrO2 skeleton in the ablation center was prone to be peeled off by the flame flow, resulting in the higher linear ablation rate of C/C-ZrC-SiC composites. The oxide layers of ZrO2 and SiO2 were formed on the transition and brim region of C/C-ZrC-SiC composites and acted as effective heat and oxygen barriers. For C/C-SiC composites, the C-SiC matrix was severely depleted in the ablation center and the formed SiO2 layer in the brim region could protect the matrix against further ablation.

Preparation and Mechanical Properties of C/C-ZrC Composites

Influence of ZrC Content on Mechanical Properties of C/C- ZrC Composites

Synthesis and Anti-ablation Properties of in Situ ZrC Modified Carbon/Carbon Composites

Oxidation and ablation behaviours of ZrC modified carbon/carbon composites

Effect of preset interfacial ZrB 2 particles on the microstructure and properties of C/C-AlSi composites

Effect of Preset Interfacial ZrB2 Particles on the Microstructure and Properties of C/C-AlSi Composites

ZrC Modified Carbon/carbon Composites Using ZrSi2 and Zr-Cu Alloys As Reactive Infiltrating Materials: A Comparative Investigation

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Influence of a Pre-Coated Pyrocarbon Layer on the Microstructure and Mechanical Properties of ZrC-doped C/C Composites

Preparation of Compact ZrC-SiC Ceramic Matrix from Thermoset Precursors for C/C-ZrC-SiC Composites with High Mechanical Properties

Effect of ZrC Content on the Properties of Biomorphic C–ZrC–SiC Composites Prepared Using Hybrid Precursors of Novel Organometallic Zirconium Polymer and Polycarbosilane

Effect of ZrO2 Morphology on the Ablation Resistance of Carbon/carbon Composites Containing ZrC Prepared by the Carbothermal Reduction Reaction

Effect Of Zrc Amount And Distribution On The Thermomechanical Properties Of C-F/Sic-Zrc Composites

Microstructures and Mechanical Properties of ZrCP/W Composites at Room Temperature

A Novel Coating Method to Fabricate ZrC Reinforced Metal Matrix Composite Cladding

Effect of Zrc Content on Microstructure and Properties of Tungsten Materials

Microstructure And Mechanical Properties Of Zrb2-Based Composites With Laminated Structure

Preparation of Co-Deposited C/C-Zrc Composites by Clvd Process and Its Properties

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Preparation and Electrical Characterization of Carbon Nanotube /zro2composite Ceramics

Microstructure and thermal conductivity of carbon/carbon composites containing zirconium carbide