Abstract:ZrC has high melting point and high hardness, and SiC-ZrC composite has excellent oxidation resistance properties. Using the toughening mechanisms of carbon fiber, C-f/ZrC-SiC ultra-high temperature Composite has become a researching focus in high-temperature materials. In this paper, the ratio of ZrC: SiC in the matrix was 2:1, 4:1, 8:1 and 16:1. The composite materials with SiC coating were tested with plasma wind tunnel ablation under the condition of 2700 K and 600 s, in order to assess the microstructures and ablation behaviors of different composite materials. The composition and microstructure of the ablated samples were characterized by XRD, SEM and EDS, respectively. The results show that at the central area at 2700 K, SiC on the surface is rapidly oxidized, while oxidation and ablation begin to occur in the matrix. The higher the Zr content in the matrix is, the better oxidation and ablation resistance are. The ablation layer is thick, even up to a millimeter level. As the Si content increases, it produces more SiO2 which is easy to volatilize under the surface. The porosity in the ablation layer increases due to evaporation of SiO2, and then oxygen will be easier to go to the interior, which result in more severe erosion. Meanwhile, oxidized ZrO2 from ZrC in the matrix is fewer. The protection of carbon fiber decreases, and it is the reason why the ablation of the carbon fiber is more serious.

Oxidation and ablation behaviours of ZrC modified carbon/carbon composites

Synthesis and Anti-ablation Properties of in Situ ZrC Modified Carbon/Carbon Composites

Effect of ZrO<SUB>2</SUB> from the Oxidation of ZrC on Ablation of ZrC Modified Carbon/Carbon Composites: Effect of ZrO<SUB>2</SUB> from the Oxidation of ZrC on Ablation of ZrC Modified Carbon/Carbon Composites

Ablation Behavior and Mechanism of C/C-ZrC Composites under Oxyacetylene Torch Flame

The effect of zirconium carbide on ablation of carbon/carbon composites under an oxyacetylene flame

Oxidation And Ablation Resistance Of C-F/Zrc-Sic Ultra-High Temperature Composites

Effect of ZrO2 Morphology on the Ablation Resistance of Carbon/carbon Composites Containing ZrC Prepared by the Carbothermal Reduction Reaction

Microstructure and ablation behavior of C/C composites doped with ZrB2

Ablation Property and Mechanism of ZrC-Cu-C/C Composites

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Microstructure and ablation properties of carbon/carbon composites modified by ZrSiO4

Oxidation Behavior of Co-Deposited ZrC Modified C/C Composites Prepared by Chemical Liquid-Vapor Infiltration Process

Microstructures and Ablative Properties of ZrC Coating by Chemical Vapor Deposition

Zrc Ablation Protective Coating for Carbon/Carbon Composites

Microstructure and ablation properties of zirconium carbide doped carbon/carbon composites

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Effects of Oxidizing Species on Ablation Behavior of C/C-Zrb2-Zrc-Sic Composites Prepared by Precursor Infiltration and Pyrolysis

Effect of yttrium carbide on ablation behavior of zirconium carbide modified carbon/carbon composites