Abstract:Chemical liquid vapor deposition (CLVD) process has got much attention because of its high efficiency and flexibility, but almost no reports are available in the fields of C/C-UHTCs preparation and the study of process parameters. In this work, CLVD-processed C/C-ZrC composites were fabricated at temperatures from 800 to 1100 degrees C, and the effects of temperature on the densification behavior and ablation property were discussed. Results displayed the mass gain, the deposition rate and the density uniformity were enhanced when the temperature increased from 800 to 900 degrees C, and thereafter they were reduced with the further arising temperature. Meanwhile, there were two different deposition modes due to the various temperatures. When the temperature was 900 degrees C, the sample possessed a good densification behavior, leading to a high density, great content of ZrC and homogenous distribution. These advantages promote a complete and dense ZrO2 coating on the sample surface during ablation, which plays as an obstacle for oxidizing species diffusion and heat transfer. Thus, the specimen prepared at 900 degrees C exhibited an outstanding anti-ablation property. However, the densification behavior was deteriorated with the further increasing temperature. Especially, when the temperature increased to 1100 degrees C, the composites had a poor density, low content of ZrC and bad dispersion of ceramics. As a result, a loose and discontinuous oxide coating was formed on the ablation surface, and the oxidation and mechanical corrosion were severe, suggesting a poor ablation resistance.

Preparation of Co-Deposited C/C-Zrc Composites by Clvd Process and Its Properties

Oxidation Behavior of Co-Deposited ZrC Modified C/C Composites Prepared by Chemical Liquid-Vapor Infiltration Process

Synthesis and Anti-ablation Properties of in Situ ZrC Modified Carbon/Carbon Composites

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process

Microstructure and Ablation Property of C/C-ZrC-SiC Composites Fabricated by Chemical Liquid-Vapor Deposition Combined with Precursor Infiltration and Pyrolysis

Effects of Joint Processes of Clvd and Pip on the Microstructure and Mechanical Properties of C/C-Zrc Composites

Influence of a Pre-Coated Pyrocarbon Layer on the Microstructure and Mechanical Properties of ZrC-doped C/C Composites

Oxidation and ablation behaviours of ZrC modified carbon/carbon composites

Influence of CLVD Thermal Gradient on the Deposition Behavior, Microstructure and Properties of C/C-ZrC Composites

Effect of ZrO2 Morphology on the Ablation Resistance of Carbon/carbon Composites Containing ZrC Prepared by the Carbothermal Reduction Reaction

Preparation And Ablation Properties Of Zrc-Tac Co-Deposition Coating For Carbon-Carbon Composites

Microstructure and ablation properties of zirconium carbide doped carbon/carbon composites

Densification Behavior and Ablation Property of C/C-ZrC Composites Prepared by Chemical Liquid Vapor Deposition Process at Temperatures from 800 to 1100 °C

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Preparation and Microstructure of Carbon/Carbon Composites Modified with Zr-Ti-C Fabricated by Reacted Melt Infiltration

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

C/C–ZrC Composite Prepared by Chemical Vapor Infiltration Combined with Alloyed Reactive Melt Infiltration

Zrc Ablation Protective Coating for Carbon/Carbon Composites

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Preparation and properties of C/C-ZrC-SiC-ZrB2 composites via polymer infiltration and pyrolysis

Microstructures and Ablative Properties of ZrC Coating by Chemical Vapor Deposition