Improvement of Fatigue Resistance for Multilayer Lead Zirconate Titanate (Pzt)-Based Ceramic Actuators by External Mechanical Loads
Gang Yang,Zhenxing Yue,Ye Ji,Xiangcheng Chu,Longtu Li
DOI: https://doi.org/10.1063/1.3042226
IF: 2.877
2008-01-01
Journal of Applied Physics
Abstract:The influence of external compressive loads, applied along a direction perpendicular to polarization, on fatigue behaviors of multilayer lead zirconate titanate (PZT)-based ceramic actuators was investigated. Under no external mechanical load, a normal fatigue behavior was observed, demonstrating that both switching polarization (Pswitching) and remnant polarization (Pr) progressively decreased with increasing switching cycles due to domain pinning by charge point defects. However, an anomalous enhancement in both switching and remnant polarizations was observed upon application of the external compressive loads. After 5×106 cycles of polarization switching, Pswitching and Pr increase by about 13% and 6% at 40 MPa, respectively, while Pswitching and Pr increase by about 11% and 21% at 60 MPa, respectively. The improvement of fatigue resistance can be attributed to non-180° domain switching and suppression of microcracking, triggered by external mechanical loads.