Abstract:By performing standard PUND (positive-up-negative-down), hysteresis-loop and dielectric measurements on the ferroelectric lead zirconate titanate (PZT) thin-film capacitors subject to bipolar/unipolar electrical cycling, we show that unipolar fatigue is evident though still less severe than bipolar fatigue conducted at the same voltage. That has been attributed to polarization retention (backswitching) induced by the residual depolarization field between the monopolar pulses where the applied field is lower than the depolarization field, and explained using the LPD-SICI model (LPD-SICI stands for local phase decomposition caused by switching-induced charge injection). The conventional view that switching does not occur during unipolar electrical cycling may need to be corrected. PUND results recorded using the pulses of the same voltage as those for repetitive fatigue cycling are not reliable if the voltage is lower than 2Vc (Vc is the saturated coercive voltage). Dielectric measurements or hysteresis-loop measurements at higher voltages (e.g. 4Vc) are more reliable ways to evaluate the degree of fatigue and could provide more valuable information in such situations. Finally, dielectric results have been used to estimate the effective thickness di of the fatigue-induced degraded (pyrochlorelike) interfacial layer after bipolar/unipolar fatigue, which has not been done so far to our best knowledge. The fact that di is still much less than the film thickness even after the most severe bipolar fatigue strongly suggests that polarization fatigue in ferroelectrics is an interface effect, not a bulk one.

Effect of polarization fatigue on the Rayleigh coefficients of ferroelectric lead zirconate titanate thin films: Experimental evidence and implications

Polarization Fatigue in Antiferroelectric (pb,la)(zr,ti)o3 Thin Films: the Role of the Effective Strength of Driving Waveform

Bipolar and unipolar electrical fatigue in ferroelectric lead zirconate titanate thin films: an experimental comparison study

Fatigue Mechanism Verified Using Photovoltaic Properties of Pb(Zr0.52Ti0.48)O3 Thin Films

Polarization Fatigue in Ferroelectric Thin Films and Related Materials

Polarization Fatigue Of Ferroelectric Pb(Zr0.1ti0.9)O-3 Thin Films: Temperature Dependence

Polarization fatigue of ferroelectric Pb(Zr_xTi_(1-x_)O_3 thin films revisited

Rayleigh-Like Nonlinear Dielectric Response And Its Evolution During Electrical Fatigue In Antiferroelectric (Pb,La)(Zr,Ti)O-3 Thin Film

Effect of Fatigue on the Pyroelectric and Dielectric Properties of PZT Films

Effects of annealing treatment on fatigue recovery of lead zirconate titanate thin films

Polarization Fatigue in Ferroelectric Vinylidene Fluoride and Trifluoroethylene Copolymer Thin Films

Effective Driving Voltage on Polarization Fatigue in (Pb,la)(zr,ti)o-3 Antiferroelectric Thin Films

Polarization fatigue mechanism of laminated hafnium zirconium oxide ferroelectric thin films

Non-destructive investigation of microstructure evolution due to ferroelectric fatigue in PLZT ceramics

Local Phase Decomposition As A Cause Of Polarization Fatigue In Ferroelectric Thin Films

Genuine driving voltage on polarization fatigue in (Pb,La)(Zr,Ti)O3 antiferroelectric thin films

Size Effect and Fatigue Mechanism in Ferroelectric Thin Films

Charge Injection and Polarization Fatigue in Ferroelectric Thin Films

Effects of Pb Excess and Temperature on Polarization Fatigue in Sol-Gel Derived Pb(Zr0.3ti0.7)O3 Thin Films

Effect of polarization fatigue on the electrocaloric effect of relaxor Pb 0.92 La 0.08 Zr 0.65 Ti 0.35 O 3 thin film

Effect of Polarization Fatigue on the Electrocaloric Effect of Relaxor Pb0.92La0.08Zr0.65Ti0.35O3 Thin Film