Abstract:The plates of four diesel engine exhaust valves used in a truck failed when servicing for 2000 h, which are made of 5Cr21Mn9Ni4N (21-4N) heat resistant alloy. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction were performed on the plate material of the failed valves and a new valve. The results show that the plate material before service is composed of first carbides (Cr23C6) and γ austenite matrix. However, appearance of the lamellar structure and plate-like precipitates within the grain is the general metallurgical features of the plate material of the failed valves, which indicates that the austenite matrix decomposed in service. XRD and electron diffraction results demonstrate that the lamellar structure is mainly composed of Cr23C6 and γ austenite, coexisting CrN phase, which formed by the discontinuous precipitation mechanism. Electron diffraction shows that the convex lens-like CrN phases precipitate within the grain, which formed by the continuous precipitation mechanism. Fractographic studies indicate that the fatigue is the dominant failure mechanism of the three valves and burning-through occurred on the plate of another failed valve. Formation of the lamellar structure and plate-like precipitations within the grain is mainly responsible for the failure of the valves. Isothermal aging tests were conducted on the plate material from the new valve to study the material stability at high temperatures. The microstructure development during aging was observed by SEM and optical microscopy. The influence of the microstructure on the service properties was discussed and possible failure causes of the valves were assessed.

Cause Analysis of Cracking of a Plug in Low Pressure Bypass Valve

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Fracture failure analysis on Alloy783 bolts in medium-pressure valve bonnets of USC units

Cause Analysis and Improvement Measures for Pipeline Cracking of 9Cr-1Mo Material

Failure Analysis of Weld Cracking in a Thick-Walled 2.25Cr-1Mo Steel Pressure Vessel

Fracture Analysis on A Cylindrical Shell Section of the Low-Pressure Absorption Tower

Failure Analysis of CRDINiCr Butterfly Valves for Nuclear Power Plant Applications

Root Cause Analysis for Cracked Pipe in Auxiliary System in Nuclear Power Plant

Fracture analysis of high pressure main steam valve stem of a 300 MW steam turbine

Analysis of Surface Cracks on TP347H Stainless Steel Tube

Failure analysis of the 304SS nut in rural atmosphere

Failure analysis on fracture causes of stainless-steel studs in seawater system of nuclear power plants

Analysis for a crack of the manhole in a reactor of Ethidene Diamine unit

Cause Analysis and Preventive Measures against Cracks in 15Cr1Mo1V Steel Welded Joint in Service

Failure analysis of 2205 duplex stainless steel connecting pipe for composite plate pressure vessel in a high pressure gas field

Crack cause analysis of a third stage stator vane of the low-pressure compressor in an aeroengine

Failure Analysis on Cracking of a HMn58-2 Copper Cooler

FRACTURE ANALYSIS OF STAINLESS STEEL WIRE OF AIR FILTER

CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE

Influences of Microstructure on Service Properties of 5cr21mn9ni4n Heat Resistant Alloy

Failure Analysis on Abnormal Cracking of Water Drain Valves in Aircraft Fuel System