Effect of on-site service for 16,000 and 38,000 h on microstructure and mechanical properties of austenitic steel HR3C reheater tubes
Ziyi Gao,Zhengfei Hu,Jie Zhang,Jianyong Wang,Zhen Zhang
DOI: https://doi.org/10.1016/j.engfailanal.2023.107247
IF: 4
2023-04-25
Engineering Failure Analysis
Abstract:The microstructure and mechanical properties of austenitic heat-resistant steel HR3C reheater steam tubes were extensively investigated after 16,000 and 38,000 h exposure at 623 °C/7.2 MPa. The surfaces of the tubes are mildly oxidized, and the oxidation layers grew slowly with service time. Metallographic observation shows that only M 23 C 6 carbides formed at the grain boundaries (GBs) and fine NbCrN nitrides that precipitated dispersedly in the matrix after 16,000 h in service. When service time up to 38,000 h, σ phases, (Cr 3 Ni 2 Si)C carbides precipitated at GBs. The large σ phase precipitated preferentially at the triangular GBs. The (Cr 3 Ni 2 Si)C carbides precipitated by the M 23 C 6 particles or formed inside the σ phases at the GBs. In addition, granular and needle-like M 23 C 6 carbides formed in the matrix, and more of them precipitated close to GBs. With service time prolonged, the precipitates close to the tube walls became plainly denser and larger. The mechanical test results indicate that the strength and hardness of the tubes increased with service time, but plasticity and impact toughness decreased. The large σ phases precipitated at the triangular GBs and M 23 C 6 carbides obvious coarsened at GBs led to the degradation trend, specially deteriorated the tube surface performance.
engineering, mechanical,materials science, characterization & testing