Abstract:ABSTRACTThe 12% Cr heat-resistant steel used for critical components of fossil-fired power plants works in high-temperature and high-pressure steam environments for a long time and inevitably undergoes a certain amount of plastic deformation during service. This plastic deformation will affect the microstructure and hot ductility of the heat-resistant steel and ultimately influence its service life. Therefore, the effect of hot compression deformation on microstructural evolution at 650°C was investigated in this work. As the amount of hot compression deformation increased, the number of subgrains significantly increased, and their sizes gradually decreased. When the amount of deformation reached 50%, dynamic recrystallization occurred, forming a preferred orientation in the rolling direction. <111> and <001> fiber texture appeared in the microstructure when the deformation amount reached 8%, and the intensity of <111> texture was significantly higher than that of <001> texture. Their intensity values further increased with the increase of the amount of deformation. As the amount of hot compression deformation increased, the deviation angle of the Kurdjumov–Sachs (KS) orientation relationship between M23C6 particles and α-Fe gradually increased. Their KS orientation relationship began to be disrupted at the deformation amount of 6% and was completely destroyed at the deformation amount of 20%. With the amount of deformation increasing up to 50%, there were no micropores at the M23C6/matrix interfaces, and no hot cracking occurred. This was mainly attributed to the occurrence of dynamic recrystallization which alleviated stress concentration at the particles /matrix interfaces. The mechanisms of microstructural evolution involving subgrains, grain boundary characteristics, texture evolution, strain distribution, and orientation relationship were discussed in detail.

The Morphological and Compositional Changes of the Carbides in F12 Heat-Resistant Alloy Steel for Long-Term Service at Elevated Temperature

An Investigation of the Embrittlement in X20crmov12.1 Power Plant Steel after Long-Term Service Exposure at Elevated Temperature

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Identification of the Precipitates by TEM and EDS in X20CrMoV12.1 after Long-Term Service at Elevated Temperature

Embrittlement of X20CrMoV12.1 Heat-resistant Alloy Steel for Long Term Exposure at Elevated Temperature

Revealing influence of warm bending on creep performance of heat-resistant 2.25Cr-1Mo-0.25 V steel

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Study on performance degradation of main steam pipe of X20CrMoV12.1 steel for long-term service

Cyclic Softening Properties of 30cr2mov Steel at Elevated Temperatures

Influence of 12Cr1MoV Material on Tissue Properties at High Temperature and Long Operating Time

Microstructure evolution and performance evaluation of T122 steel before and after service

Structural Changes of 12cr1movg Steel During High-Temperature Creep

Creep Behavior and Cavitation Evolution of 15crmog Steel at High Temperatures

Microstructural Evolution of a Re-Containing 10% Cr-3Co-3W Steel during Creep at Elevated Temperature

Exploring Carbide Evolution in Bainitic 2.25cr1mo Steel Subjected to Creep Rupture Tests

Microstructural evolution in austenitic heat-resistant cast steel 35Cr25Ni12NNbRE during long-term service

Microstructural Evolution of X20CrMoV12.1 Steel Upon Short-term Creep Rupture Test

Microstructural Evolution in 12% Cr Heat-Resistant Steel During Compression Deformation at 650°C

High-temperature Creep Behavior of 12cr1movg Steel

Evolution and Coarsening of Carbides in 2.25Cr-Lmo Steel Weld Metal During High Temperature Tempering

Microstructure-Property Relationship and Embrittlement Mechanism of HR3C Steel with High-Temperature Service of 65000 h