Failure analysis of stainless steel metal hose in welding
Youngsik Kim,Byunghak Choe,Sunghee Han,Daehyun Kim,Jinha Kim,Kwangsoo Choi,Hunbae Kim,Seokyeol Choi
DOI: https://doi.org/10.1016/j.engfailanal.2024.108540
IF: 4
2024-06-15
Engineering Failure Analysis
Abstract:While using ammonia (NH 3 ) gas at 10 bar/500°C, a stainless steel 304 metal hose used as a bellow expansion joint was fractured. It was observed that the fracture of the metal hose started near the weld between the hose and the flange, and progressed to approximately 1/4 of the circumference of the weld. No metallurgical defects were found in the weld where the crack occurred. However, the folded part of the metal hose is welded to the flange, which can cause cracks. In other words, when the metal hose is forcibly compressed or stretched in order to weld it to the flange, the stress concentration by work hardening including residual stress cause the metal hose to become brittle or crack. It is determined that when a high strain cyclic load or torsional deformation is applied to a high-hardness metal component, the metal hose will reach fatigue failure in a short period of time.
engineering, mechanical,materials science, characterization & testing