Failure analysis of the 304SS nut in rural atmosphere

Menghao Liu,Zhigao Wang,Fangyuan Lu,Cuiwei Du,Xiaogang Li

DOI: https://doi.org/10.1016/j.engfailanal.2023.107632

IF: 4

2023-09-17

Engineering Failure Analysis

Abstract:An unexpected cracking of a 304SS nut exposed to a rural atmosphere caused gas leakage. Aiming at identifying the failure cause, this study has conducted crack morphology analysis and corrosion product analysis using X-ray computed tomography, electron backscatter diffraction, and scanning electron microscope. The results revealed that the primary failure is attributed to intergranular corrosion cracking, where corrosion has played a predominant role. Initial corrosion was induced by MnS inclusions and chromium carbides. The application of additional force during re-examination promoted crack propagation. MnS inclusions played an auxiliary role in crack propagation due to the high stress concentration around them. The main contributing factor to the failure is the unqualified material, which contains excessive amounts of carbon and sulfur, significantly reducing the corrosion resistance and toughness. Based on these findings, recommendations for preventing further failures were proposed. This study has provided a failure case in mild environment and demonstrate that failure of 304SS would also occur even if the environment is the rural atmosphere, as long as the material is sensitized.

engineering, mechanical,materials science, characterization & testing