Abstract:A shell and tube heat exchanger had failed its four tubes after just over a year in service. One of these tubes was analyzed in this examination. This heat exchanger is used to transfer heat from steam on the shell side to slurry on the tube side. The tube material was made of SA 249 TP 304L, a standard specification for welded austenitic stainless steel tubes. A failure investigation was carried out on the leaked tubes by performing a number of examinations including visual and macroscopic examination, chemical analysis, metallographic examination, hardness testing and scanning electron microscopy equipped with energy-dispersive spectroscopy analysis. Results of the failure analysis showed that the leaked tubes of the heat exchanger had primarily experienced stress-corrosion cracking (SCC) in the longitudinal direction caused by the combined effects of tensile stress and corrosion. Most of the stress-corrosion cracks initiated at multiple sites of the external surface of the tubes where corrosion pits and other surface defects were present. Formation of surface defects was most likely associated with some excessive contact and/or collision between tube and adjacent tubes or with baffles or other support in the heat exchanger. In the early stage, most of the cracks were not branched, but later continued by cracks branching in transgranular manner. Some of the trace elements found on the fracture surface deposit may have been responsible for the formation of corrosion pits and SCC on the tubes, acting either alone or in combination. In addition, at location close to the multiple parallel cracks in the longitudinal direction, the tube also experienced other multiple parallel cracks, but in its circumferential direction. None of these cracks had reached the internal wall of the tube.

Corrosion Failure of Stainless Steel Tube During Storage

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Behavior of Corroded Thin-Walled Concrete-Filled Steel Tubular Stub Columns

Failure Analysis of Stainless Steel Heat Exchanger Tubes in a Petrochemical Plant

Analysis of the causes of the cracking of tube bundles of 316L stainless steel Shell-and-Tube heat exchanger

Failure analysis of heat exchange tubes in hydrogenation unit

Failure analysis of 316L stainless steel corrugated pipe

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Failure analysis on fracture causes of stainless-steel studs in seawater system of nuclear power plants

Failure Analysis of the High Nitrogen Austenitic Stainless-Steel Boiler Tank Weldments

Analysis of Corrosion Failure of 20# Steel Tubular Induction Probe in Simulated Environment of a Gas Field

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

The Stress Corrosion Cracking of Austenitic Stainless Steel Heat Exchange Tubes: Three Cases Study

Failure analysis of a high strength Cr-containing tube used in an oil well

The Failure Mechanism of the 316 SS Heat Exchanger Tube in the Geothermal Water Environment

Correlation between Laboratory-Accelerated Corrosion and Field Exposure Test for High-Strength Stainless Steels

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block

Failure analysis of crevice corrosion on 304 stainless steel tube heat exchanger

Failure analysis of a 304 stainless steel heat exchanger in liquid sulfur recovery units

Experimental study on mechanical properties and low-cycle fatigue behaviour of stainless steels subjected to salt spray and dry/wet cycle