Abstract:A shell and tube heat exchanger had failed its four tubes after just over a year in service. One of these tubes was analyzed in this examination. This heat exchanger is used to transfer heat from steam on the shell side to slurry on the tube side. The tube material was made of SA 249 TP 304L, a standard specification for welded austenitic stainless steel tubes. A failure investigation was carried out on the leaked tubes by performing a number of examinations including visual and macroscopic examination, chemical analysis, metallographic examination, hardness testing and scanning electron microscopy equipped with energy-dispersive spectroscopy analysis. Results of the failure analysis showed that the leaked tubes of the heat exchanger had primarily experienced stress-corrosion cracking (SCC) in the longitudinal direction caused by the combined effects of tensile stress and corrosion. Most of the stress-corrosion cracks initiated at multiple sites of the external surface of the tubes where corrosion pits and other surface defects were present. Formation of surface defects was most likely associated with some excessive contact and/or collision between tube and adjacent tubes or with baffles or other support in the heat exchanger. In the early stage, most of the cracks were not branched, but later continued by cracks branching in transgranular manner. Some of the trace elements found on the fracture surface deposit may have been responsible for the formation of corrosion pits and SCC on the tubes, acting either alone or in combination. In addition, at location close to the multiple parallel cracks in the longitudinal direction, the tube also experienced other multiple parallel cracks, but in its circumferential direction. None of these cracks had reached the internal wall of the tube.

Failure analysis of a 304 stainless steel heat exchanger in liquid sulfur recovery units

Failure Analysis of Stainless Steel Heat Exchanger Tubes in a Petrochemical Plant

Analysis of the causes of the cracking of tube bundles of 316L stainless steel Shell-and-Tube heat exchanger

The Failure Mechanism of the 316 SS Heat Exchanger Tube in the Geothermal Water Environment

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

The Stress Corrosion Cracking of Austenitic Stainless Steel Heat Exchange Tubes: Three Cases Study

Failure analysis of heat exchange tubes in hydrogenation unit

Failure analysis of crevice corrosion on 304 stainless steel tube heat exchanger

Stress Corrosion Cracking of Heat Exchanger Tubes in District Heating System

Corrosion Failure Analysis for Heat Transfer Tube in Quick Cooled Oil-Dilute Steam Heat Exchanger

Failure analysis of sulphidation-oxidation corrosion of Incoloy 800HT superheater tube

Failure Analysis on Abnormal Corrosion of Economizer Tubes in a Waste Heat Boiler

Failure analysis of one peculiar ‘Yin-Yang’ corrosion morphology on heat exchanger tubes in purified terephthalic acid (PTA) dryer

A laboratory study of the failure analysis of copper tube used in the air conditioning heat exchanger

Failure Analysis on Abnormal Bursting of Heat Transfer Tubes in Spiral-Wound Heat Exchanger for Nuclear Power Plant

Erosion and intergranular corrosion induced failure of S31254 stainless steel – Case study on Venturi scrubber in a natural gas purification plant

Failure analysis of reheater tubes in a 350 MW supercritical circulating fluidized bed boiler

Analysis of Causes and Protective Measures against Corrosion Perforation in the Shell-Side Outlet Flange of a Sour Water Steam Heater

Failure Analysis on Abnormal Leakage of Shell and Tube Heat Exchanger in Specialty Chemical Plant

Failure Analysis of Duplex Stainless Steel for Heat Exchanger Tubes with Seawater Cooling Medium