Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

Fracture Mechanics Analysis Of The Stress Corrosion Cracking Failure Of Stainless Steel Hexagonal Head Screws In A Marine-Industrial Environment

Investigation of stress corrosion cracking behavior and mechanism analysis of a 1900 MPa-grade ultra-high-strength stainless steel

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Stress Corrosion Cracking of 316l Haz for 316l Stainless Steel/Inconel 52m Dissimilar Metal Weld Joint in Simulated Primary Water

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Evaluation of Stress Corrosion Cracking Susceptibility of Forged 316 Stainless Steel in Simulated Primary Water

Study on the Cracking Behavior of Fasteners in Long-Term Service under Marine Environment

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

Evaluation Of Stress Corrosion Cracking Of Type 304l Stainless Steel In Low Concentration Sodium Hydroxide Solution With High Temperature

Electrochemical Evaluation of Stress Corrosion Cracking Susceptibility of Ti-6Al-3Nb-2Zr-1Mo Alloy Welded Joint in Simulated Deep-Sea Environment

Failure analysis on fracture causes of stainless-steel studs in seawater system of nuclear power plants

Investigation of Multi-Factor Stress Corrosion Cracking Failure of Safe-End Feedwater Lines of Submarine Power System

Corrosion and Stress Corrosion Cracking Susceptibility of Type 347H Stainless Steel in Supercritical Water

STRESS CORROSION CRACKING BEHAVIOR OF A NEW KIND OF ULTRAHIGH STRENGTH STEEL Cr12Ni4Mo2Co14 IN ACID ENVIRONMENT

Microstructurally and mechanically small fatigue crack growth behaviors of 316LN stainless steel in high-temperature pressurized water

A Three-Dimensional Model of Non-Slipping Stress Corrosion Cracking under Low Loads

Stress Corrosion of Austenitic Stainless Steel 316L in High Temperature Water

Effects of Chloride and Oxygen on Stress Corrosion Cracking of Cold Worked 316/316L Austenitic Stainless Steel in High Temperature Water

Stress Corrosion Cracking in the Heat Affected Zone of A Stainless Steel 308L-316L Weld Joint in Primary Water

Stress Corrosion Cracking Behavior of FV520B Stainless Steel Exposed to Aqueous H2S+Cl-Environment