Abstract:Stress corrosion cracking is one of the most dangerous types of corrosion damage in metallic materials. We present the results of studying the impact of environmental factors on the susceptibility of AMg6 aluminum alloy and 12Kh18N10T stainless steel to stress corrosion cracking under four-point bending. Tests of loaded samples were carried out in laboratory and field conditions of the moderately warm climate of the coastal zone over a period of six months. The samples were examined daily with fixation of the time to their destruction and upon completion of the tests the appearance of the samples and the depth of intergranular corrosion on microsections were assessed. A 3D relief was constructed using macro photography of the surface with the determination of the depth of corrosion foci. We also carried out a comparative analysis of the frequency of stress-induced destruction of steel samples of various grades both in atmospheric and laboratory conditions. It is shown that in atmospheric conditions characterized by the presence of dust particles acting as concentrators for the formation of corrosion foci, the aggressiveness of the corrosive effect of the environment increases, whereas the general corrosion resistance of materials decreases. The most pronounced effect of the environment was recorded in AMg6 alloy samples when exposed under a ventilated canopy in conditions of periodic spraying of seawater aerosols. The depth of surface corrosion damage was up to 0.1 mm. When the test samples were exposed under other conditions (salt fog chamber and louvered storage) the corrosion damage was absent. The results obtained can be used to predict the corrosion resistance of the products made of AMG6 alloy and 12Kh18N10T steel when operated in conditions of loading under the impact of environmental factors.

Stress Corrosion Cracking of Metals and Alloys in Aggressive H2S–CO2–Cl– Environments

Effect of CO2/H2S and Applied Stress on Corrosion Behavior of 15cr Tubing in Oil Field Environment

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Corrosion fatigue of 16Mn pressure vessel steel in H(2)S environment

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: Initial corrosion with tensile stress coupling

Criteria for Revaluating the Propensity of Metals to Corrosion Cracking during Accelerated Testing in an Environment with Hydrogen Sulfide and Carbon Dioxide

Stress corrosion tests for prestressing steels—Part 1: The influence of surface condition and test solution composition on hydrogen charging

Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure

Corrosion fatigue of 16Mn pressure vessel steel in H2S environment

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Effect of Temperature and Pressure on Corrosion and Hydrogenation of Steel in Chloride-Acetate Environment with Different Concentrations of Hydrogen Sulfide and Carbon Dioxide

Effect of Hydrogen Sulfide Containing Environment on the Characteristics of Strength, Cyclic Endurance and Magnetic Properties of Cr – Mo – V – Nb Pipe Steel

Corrosion Activity of Operating Conditions for the Steel Equipment and Pipelines in the Plants Extracting CO2-Containing Gases

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: understanding electrochemical corrosion with tensile stress coupling

Pitting corrosion and stress corrosion cracking study in high strength steels in alkaline media

Pitting Corrosion of Supermartensitic Stainless Steel in Chloride Solutions Containing Thiosulfate or H2S

Study of the corrosion resistance of aluminum alloy AMg6 and steel 12Kh18N10T in conditions of loading under the impact of environmental factors

Stress Corrosion Cracking Behavior of FV520B Stainless Steel Exposed to Aqueous H2S+Cl-Environment

Corrosion Degradation of Long-Term Operated Steel Sewer Pipes

Effects of H2S/HS− on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions