Abstract:Extended exposure to seawater results in the erosion of the structural high-strength steels utilized in marine equipment, primarily due to the infiltration of hydrogen. Consequently, this erosion leads to a decrease in the mechanical properties of the material. In this investigation, the mechanical responses of Q690 structural high-strength steel specimens were investigated by considering various hydrogen charging parameters, such as the current density, charging duration, and solution concentration values. The findings highlighted the significant impacts of electrochemical hydrogen charging parameters on the mechanical behaviors of Q690 steel samples. Specifically, a linear relationship was observed between the mechanical properties and the hydrogen charging current densities, while the associations with the charging duration and solution concentration were nonlinear. Additionally, the fracture morphology under various hydrogen charging parameters was analyzed and discussed. The results demonstrate that the mechanical properties of the material degrade with increasing hydrogen charging parameters, with tensile strength and yield stress decreasing by approximately 2-4%, and elongation after fracture reducing by about 20%. The findings also reveal that macroscopic fractures exhibit significant necking in uncharged conditions. As hydrogen charging parameters increase, macroscopic necking gradually diminishes, the number of microscopic dimples decreases, and the material ultimately transitions to a fully brittle fracture.

Stress corrosion tests for prestressing steels—Part 1: The influence of surface condition and test solution composition on hydrogen charging

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Influence of hydrogen ingress on residual stress and strain in pipeline steels

Effect of Hydrogen Charging on the Mechanical Properties of High-Strength Copper-Base Alloys, Austenitic Stainless Steel AISI 321, Inconel 625 and Ferritic Steel 1.4511

Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive films on X70 micro-alloyed steel

Hydrogen embrittlement of 2205 duplex stainless steel in in-situ tensile tests

The effect of acidification on hydrogen uptake and corrosion resistance of advanced high-strength steels

Diffusible Hydrogen Facilitated Stress Corrosion Cracking in 316 Stainless Steel Using In-Situ Gaseous Hydrogen Charging in Simulated PWR Environment

Evaluating the Effect of Hydrogen on the Tensile Properties of Cold-Finished Mild Steel

Scanning Kelvin Probe Investigation of High-Strength Steel Surface after Impact of Hydrogen and Tensile Strain

Effect of Hydrogen on Plastic Deformation Near Crack-tip of A537 Steel in 3.5%nacl Solution

Hydrogen Insertion into Complex-Phase High-Strength Steel during Atmospheric Corrosion at Low Relative Humidity

Galvanic Corrosion Study between Tensile-Stressed and Non-Stressed Carbon Steels in Simulated Concrete Pore Solution

Influence of Specimen Surface Roughness on Hydrogen Embrittlement Induced in Austenitic Steels during In-Situ Small Punch Testing in High-Pressure Hydrogen Environments

Synergistic effect of different testing environments on the hydrogen-induced mechanical degradation to establish the role of microstructural features on the failure of X70 pipeline steel

The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment

STRESS CORROSION CRACKING BEHAVIOR OF A NEW KIND OF ULTRAHIGH STRENGTH STEEL Cr12Ni4Mo2Co14 IN ACID ENVIRONMENT

Effect of electrochemical charging on the hydrogen embrittlement susceptibility of a low-alloyed tempered martensitic steel submitted to high internal pressure

Stress Corrosion Cracking of Metals and Alloys in Aggressive H2S–CO2–Cl– Environments

On the local evaluation of the hydrogen susceptibility of cold-formed and heat treated advanced high strength steel (AHSS) sheets

Effects of Electrochemical Hydrogen Charging Parameters on the Mechanical Behaviors of High-Strength Steel