Abstract:This paper discusses the problems of resistance of the metal of the tubing branch pipe (tubing) to the process of its destruction in a medium containing hydrogen sulfide and when exposed to external forces. A 73х73 tubing nozzle made of 38G2SFA steel was selected as the material for research. The tubing fragment was destroyed during production well operation. To establish the reasons for the failure of the tubing nozzle, a visual inspection was carried out, tests were performed to assess the hardness and mechanical properties, the microstructure and microtexture of the metal were analyzed using scanning electron microscopy (SEM) methods. To analyze the nature of the distribution of introduced defects, the mutual orientation of structural components and crystallographic texture, studies were carried out by the method electron backscatter diffraction (EBSD). Studies of the suspended branch pipe, which does not have chemical protection, showed that the cause of its destruction was hydrogen sulfide stress corrosion cracking (SSCC) as a result of hydrogen embrittlement and the action of external tensile forces exceeding the yield strength of the metal. It was established that as a result of the interaction of hydrogen sulfide of the distilled product with the metal of the branch pipe, hydrogen embrittlement of the material of the branch pipe occurred. The process of hydrogen embrittlement of the fragment was proved by detecting hydrogen blisters in the metal microstructure and establishing the process of coalescence of neighboring inclusions. In addition, the results of the test to measure the hardness of the metal along the wall thickness further supported the hypothesis of hydrogen embrittlement of the tubing. EBSD analysis showed that the threaded part of the branch pipe is characterized by a small size of structural elements and an increased density of introduced defects (geometrically necessary dislocations), which are a promising site for the deposition of molecular hydrogen. It is concluded that reaching the limit concentration of molecular hydrogen reduces the binding energy of metal atoms and this process initiates the formation of pores. It has been established that the development of cracks along large-angle grain boundaries is facilitated, and small-angle and coincidence site lattice (Σ3, Σ5, Σ11 and Σ13b) grain boundaries are active barriers to crack propagation. It has been shown that by optimizing the elemental composition of steel, controlling the microstructure, crystallographic texture, as well as the type and state of grain boundaries, new pipeline steels can be produced that are more resistant to SSCC.

Effect of Hydrogen Sulfide Containing Environment on the Characteristics of Strength, Cyclic Endurance and Magnetic Properties of Cr – Mo – V – Nb Pipe Steel

Effect of Structure and Nonmetallic Inclusions on Hydrogen Sulfide Cracking Resistance in Structural Pipe Steels

Hydrogen embrittlement of X80 pipeline steel in H 2 S environment: Effect of hydrogen charging time, hydrogen-trapped state and hydrogen charging–releasing–recharging cycles

Stress Corrosion Cracking of Metals and Alloys in Aggressive H2S–CO2–Cl– Environments

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Structure and Properties of Steel for Producing Hydrogen Sulfide Resistant Oil and Gas High Strength Pipes

FIELD EXPERIENCE OF DOWNHOLE EQUIPMENT OPERATION IN HYDROGEN SULFIDE-CONTAINING ENVIRONMENTS

RESISTANCE OF FERRITE-PERLITE STEEL TUBING BRANCH PIPE METAL TO DESTRUCTION IN HYDROGEN SULFIDE MEDIUM

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment

Corrosion Behavior and Mechanical Performance of Drill Pipe Steel in a CO2/H2S-Drilling-Fluid Environment

Hydrogen embrittlement sensitivity of dispersion-strengthened-high-strength steel welded joint under alternating wet-dry marine environment

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Effect of Hydrogen Sulfide on Pipe Steel Carbon Dioxide Corrosion

Hydrogen embrittlement susceptibility of AISI 4140 alloy-steel under cathodic protection and in H 2 S and CO 2 environment

Effect of Tensile Stress on Self-Magnetic Leakage Field in Carbon Steel Pipe Material

Hydrogen trapping and hydrogen embrittlement (HE) susceptibility of X70 grade high-strength, acid-resistant, submarine pipeline steel with Mg treatment

Combined effect of hydrogen embrittlement and corrosion on the cracking behaviour of C110 low alloy steel in O2-contaminated H2S environment

Synergistic effect of different testing environments on the hydrogen-induced mechanical degradation to establish the role of microstructural features on the failure of X70 pipeline steel

Hydrogen Embrittlement Sensitivity of X70 Welded Pipe Under a High-Pressure Pure Hydrogen Environment

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block