Abstract:Advanced lightweight high-strength steels are often compositionally and microstructurally complex. While this complex feature enables the activation of multiple strengthening and strain-hardening mechanisms, it also leads to a complicated damage behavior, especially in the presence of hydrogen (H). The mechanisms of hydrogen embrittlement (HE) in these steels need to be properly understood for their successful application. Here we focus on a high-Mn (∼20 wt.%), high-Al (∼9 wt.%) lightweight steel with an austenite (∼74 vol.%) and ferrite (∼26 vol.%) two-phase microstructure and unravel the interplay of H-related decohesion and localized plasticity and their effects on failure. We find that HE in this alloy is driven by both, H-induced intergranular cracking along austenite-ferrite phase boundaries and H-induced transgranular cracking inside the ferrite. The former phenomenon is attributed to the mechanism of H-enhanced decohesion. For the latter damage behavior, systematic scanning electron microscopy-based characterization reveals that only parts of the transgranular cracks inside ferrite are straight (∼52% proportion) and along the cleavage plane. Other portions of these transgranular cracks show a distinct deviation from the {100} planes at certain stages of crack propagation, which is associated with a mechanism transition from the H-enhanced transgranular decohesion of the ferrite by cleavage to the H-associated localized plasticity occurring near the propagating crack tip. These mechanisms are further discussed based on a detailed comparison to the damage behavior at cryogenic temperatures and on the nanoindentation results performed with in-situ H-charging. The findings provide new insights into the understanding of the interplay between different HE mechanisms operating in high-strength alloys and their synergistic effects on damage evolution.

Hydrogen embrittlement sensitivity of dispersion-strengthened-high-strength steel welded joint under alternating wet-dry marine environment

Hydrogen embrittlement of high-strength marine steel as a weld joint in artificial seawater under cathodic polarization

Embrittlement of Notched Duplex Stainless Steel: Role of Hydrogen-Assisted Void Growth and Cleavage

Impact of hydrogen embrittlement on the tensile-shear property of resistance spot-welded advanced high-strength martensitic steels

Effect of fatigue damage on the hydrogen embrittlement sensitivity of X80 steel welded joints

Effect of hydrogen on pitting corrosion of 2205 duplex stainless steel under alternating dry/wet marine environment

Promotion of pitting corrosion at hydrogen-enriched α/γ phase boundaries in austenitic stainless steel weld joints

Effects of Electrochemical Hydrogen Charging Parameters on the Mechanical Behaviors of High-Strength Steel

Effect of microstructure on hydrogen embrittlement and hydrogen-induced cracking behaviour of a high-strength pipeline steel weldment

Study on Mechanical Behaviours and Microstructure Features of Q690 Steel Weldments with Various Electrochemical Hydrogen Charging Conditions

Experimental and Modeling Analysis of Hydrogen Motion Behavior in Welding Zone of 2.25Cr–1Mo–0.25 V Steel Welded Joint with Hydrogen Corrosion

The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment

Hydrogen embrittlement behavior of Al-Si coated steel laser wire filling welding joint

Hydrogen effects on passivation and SCC of 2205 DSS in acidified simulated seawater

Hydrogen influence on some advanced high-strength steels

Hydrogen-associated decohesion and localized plasticity in a high-Mn and high-Al two-phase lightweight steel

Investigation of the hydrogen-induced cracking of E690 steel welded joint in simulated seawater

Change in Hydrogen Trapping Characteristics and Influence on Hydrogen Embrittlement Sensitivity in a Medium-Carbon, High-Strength Steel: The Effects of Heat Treatments

Effect of test temperature on the hydrogen embrittlement susceptibility of a duplex stainless steel

Improvement of Resistance to Hydrogen Embrittlement for 1300MPa Ultra-high Strength Steel by Introducing Nano-sized Cu-rich Phase Precipitation

Hydrogen-enhanced microbanding in an austenitic FeMnAlC low-density steel: Effect on hydrogen embrittlement resistance