Abstract:Flat butt welding is commonly used to construct large welded structures, such as ships. Under high temperatures during the welding process, the hydrogen-containing compound in the arc welding decomposes into monoatomic hydrogen, which is dissolved in the molten pool in large amounts. High-strength steel, widely used for large ship structures, is sensitive to welding residual stress. Non-uniform welding residual stresses in such structures could facilitate the diffusion and accumulation of hydrogen in the steel, leading to excessive hydrogen localized at the welded joints. This behavior can cause hydrogen embrittlement, threatening the safety and reliability of ship structures. In this study, based on the thermal elastic-plastic theory and the theory of residual stress-induced hydrogen diffusion, a three-dimensional finite element analysis thermodynamic model for the flat butt welding joints of high-strength steel was established, the welding process was simulated, and the distribution law for the welding residual stress field was obtained. Then the sequential coupling calculation of hydrogen diffusion was performed by defining the welding residual stress field of flat butt welding joint of high strength steel as the pre-defined field, and the hydrogen diffusion behavior under the welding residual stress field was obtained. The results revealed large residual stresses in the weld and heat-affected zone of the butt welded joints of high-strength steel plates. As the distance from the weld increased, the level of welding residual stress decreased rapidly. The welding residual stress affected the hydrogen diffusion behavior, and hydrogen was enriched in regions with high residual stress. Moreover, hydrogen-induced cracking occurred easily in the weld and heat-affected zone. These results can provide theoretical support for ensuring the safety and reliability of large ship structures.

Effect of fatigue damage on the hydrogen embrittlement sensitivity of X80 steel welded joints

Research on the hydrogen assisted fatigue damage in X80 pipeline steel welded joint

Study on the mechanical properties of X80 pipeline steel under pre-charged high-pressure gaseous hydrogen

Embrittlement of Notched Duplex Stainless Steel: Role of Hydrogen-Assisted Void Growth and Cleavage

Effects of hydrogen on the fracture toughness of X80 steel base metal and girth weld under strong cathodic current with in-situ hydrogen charging

Effects of Hydrogen and Specimen Thickness on Fracture Toughness of Ferritic Steel Welded Joint

Influence of Hydrogen Environment on Fatigue Fracture Morphology of X80 Pipeline Steel

Role of microstructure heterogeneity on hydrogen-assisted fracture toughness degradation of X80 weld metal in H 2 S-saturated solution

Effects of Hydrogen on the Mechanical Response of X80 Pipeline Steel Subject to High Strain Rate Tensile Tests

Hydrogen embrittlement of high-strength marine steel as a weld joint in artificial seawater under cathodic polarization

The Fatigue Threshold Computation Of Steel In Hydrogen Environment By Shakedown Analysis

Effect of hydrogen charging intensities and times on hydrogen embrittlement of Q&P980 steel

Effects of Sheared Edge and Overlap Length on Reduction in Tensile Fatigue Limit before and after Hydrogen Embrittlement of Resistance Spot-Welded Ultra-High-Strength Steel Sheets

Hydrogen embrittlement of X80 pipeline steel in H 2 S environment: Effect of hydrogen charging time, hydrogen-trapped state and hydrogen charging–releasing–recharging cycles

Influences of Solution Hydrogen on the Fatigue Crack Propagation Lives of TA15 Alloys Electron Beam Welded Joints

Effect of Residual Stress on Hydrogen Diffusion in Flat Butt Welding Joints

Effect of stress triaxiality on the hydrogen embrittlement micromechanisms in a pipeline steel evaluated by fractographic analysis

Investigation of the hydrogen-induced cracking of E690 steel welded joint in simulated seawater

Hydrogen embrittlement sensitivity of dispersion-strengthened-high-strength steel welded joint under alternating wet-dry marine environment

Impact of hydrogen embrittlement on the tensile-shear property of resistance spot-welded advanced high-strength martensitic steels

Effect of cathodic current density on hydrogen embrittlement susceptibility of X70 steel girth weld in different soil simulation solutions