Effect of microstructure on hydrogen embrittlement and hydrogen-induced cracking behaviour of a high-strength pipeline steel weldment

Peng Zhang,Majid Laleh,Anthony E. Hughes,Ross K.W. Marceau,Tim Hilditch,Mike Yongjun Tan
DOI: https://doi.org/10.1016/j.corsci.2023.111764
IF: 7.72
2024-02-01
Corrosion Science
Abstract:Hydrogen embrittlement (HE) and hydrogen-induced cracking (HIC) behaviour of a X65 steel pipeline weldment were investigated using slow strain rate tensile (SSRT) testing of specimens that were specifically extracted from different zones of the weldment (i.e., weld metal (WM), heat-affected zone (HAZ), and base metal (BM)). The WM was found to be the most susceptible zone to HE and HIC, while BM the least. Analysis of microstructure, fracture surface, secondary crack formation, and mechanical behaviour revealed that the high HE susceptibility of WM is correlated to microstructural features including Ti-rich inclusions, martensite/austenite (M/A) constituents, and prior austenite grain boundaries (PAGBs).
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?