Abstract:The microstructure evolution and deformation mechanisms of AZ31 alloy sheet during hot rolling were investigated. The initial microstructure in the as-received AZ31 sheet shows basal texture with an average grain size of 37μm. During the subsequent hot rolling processing, dislocation slip occurs in addition to extension, contraction and double twinning, and the twinning mode is dependent on the grain orientation, grain size and rolling temperature. Continuous dynamic recovery and recrystallization (CDRR) is the main mechanism of grain refinement for the AZ31 sheet during hot rolling, and the {−1011} contraction and {−1011}−(10−12) double twinning accelerate the refinement process. Contraction and double twinning have positive effect on grain refinement and texture randomization for the AZ31 alloy during hot rolling. In this study, higher per-pass reduction of 50% and higher rolling temperature of 400°C led to more uniform grain structure with more random texture, which resulted in the higher ductility than that of the sheet samples rolled at 300°C and at per-pass reduction of 30%. Therefore, higher temperatures and larger per-pass reduction rolling are recommended for microstructure optimization and the mechanical properties improvement of the AZ31 sheet.

Strength Enhancement of Mg–3Gd–1Zn Alloy by Cold Rolling

Anomalous Ductility-Strength Synergy Occurred after Cold Rolling in a High Gd Content Mg Alloy

Microstructure and Tensile Properties of Mg-3Al-1Zn Sheets Produced by Hot-Roller-cold-material Rolling

Strengthening Mg–8Li–3Al–2Zn-1Gd-0.2Zr alloy by combining hot extrusion and cold rolling

Improving the Ductility of Mg-2.5Nd-0.5Zn-0.5Zr Alloy by Multi-Pass Hot Rolling

Effect of Cold Deformation on Microstructure and Mechanical Properties of Mg-8Gd-3Y-0.5Zr Alloy

Effects of Gd Concentration on Microstructure, Texture and Tensile Properties of Mg–Zn–Gd Alloys Subjected to Large Strain Hot Rolling

A Rolled Mg‐8Al‐1Sm‐1Zn Alloy with High Strength‐Ductility via Single‐Pass Liner Rolling

High strength-ductility synergy and low anisotropy of Mg-4.5Al-2.6Zn-0.3Mn alloy sheet achieved by annealing after rolling

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

Microstructures and mechanical properties of high-strength Mg-Gd-Y-Zn-Zr alloy sheets processed by severe hot rolling

Microstructure and mechanical properties of hot-rolled Mg–Zn–Nd–Zr alloys

Microstructure and Mechanical Properties of Rolled Mg-12gd-3y-0.4zr Alloy Sheets

Enhancing Mechanical Properties of Rolled Mg-Al-Ca-Mn Alloy Sheet by Zn Addition

Influence of Texture and Grain Size on the Room-Temperature Ductility and Tensile Behavior in a Mg–Gd–Zn Alloy Processed by Rolling and Forging

Improving Strength and Ductility of Mg–Gd–Y–Zn–Zr Alloy Simultaneously Via Extrusion, Hot Rolling and Ageing

Effect of cold rolling on the microstructure and mechanical properties of MG-8GD-3Y-0.5ZR alloy

Strength-ductility balance of Mg-1.03Ca-0.47Mn Mg alloy sheet produced by rolling and annealing

Improved Ductility of Mg–Zn–Ce Alloy by Hot Pack-Rolling

Rolling Temperature and Subsequent Annealing on Microstructure, Texture and Mechanical Properties of Consecutive Rolled Mg-2.0zn-0.8gd Alloy

Effects of Hot Rolling Processing on Microstructures and Mechanical Properties of Mg–3%Al–1%Zn Alloy Sheet