Effect of Brazing Interface Parameters on Brazing Quality of Hard Metal

Yi WAN,Liyan CHEN,Chun XU,Chi ZHANG

DOI: https://doi.org/10.3969/j.issn.1008-1690.2013.03.007

2013-01-01

Abstract:Using high-frequency induction heating equipment and using both YG13 hard metal and 20CrMo low alloy steel as base metals,the effect of contact pressure and surface roughness the two base metals on the brazing quality was investigated by a flake cadmium-free sandwich silver-copper solder.It has been found that the interface roughness has a significant influence on the brazing quality,and the sample sand-blasted is superior to the sample sand-burnished in the brazing quality.Furthermore,the interface contact pressure has direct influence on both the thickness of silver solder and the deposition ratio of brazing.The thickness of silver solder will decrease with the increase in interface contact pressure.The deposition rate of brazing at contact pressure of 0.1 MPa is the highest as compared with that of brazing at 0.3 MPa or 0.5 MPa.