Effect Of Zirconium Addition On Microstructure And Mechanical Property Of Tic/Ti6al4v Composites

XULIANG MA,XIANG WANG,LI LI,PENGTAO GAI,CHENGWU ZHU

DOI: https://doi.org/10.1142/S0217979209060981

2009-01-01

International Journal of Modern Physics B

Abstract:TiC/Ti6Al4V composites with different Zr additions were prepared successfully in a consumable vacuum arc furnace equipped with a water-cooled copper crucible and the effect of the Zr content on the microstructure and mechanical property of 15 vol.% TiC/Ti6Al4V composites was investigated by XRD, SEM and hardness testing. The results show that when the level of Zr addition is less than 4 wt.%, the morphology of the primary TiC in the composites is dendrite, and the petal-shape, pieceshape or palpus-shape eutectic TiC separates out around the primary TiC. The average size of the primary TiC decreases and the amount of eutectic TiC increases gradually with increasing Zr content. The effects of Zr on morphology of the primary TiC weaken with further addition of Zr. And the hardness (HRC) of composites was obviously increased in the whole range of Zr addition. The refinement mechanism of Zr was attributed to the combined effects of increase in nucleation rate at the constitutionally supercooled zone ahead of the solidification front and reduction in growth rate.