Effects of Ball Milling Modes on Phase Structure of (Ti,15w,5mo,0.2v)(cn)-20Ni Composite Powders During Reaction Synthesis

王焱坤,刘颖,金永中,叶金文,刘晓波

2009-01-01

Abstract:The(Ti,15W,5Mo,0.2V)(CN)-20Ni composite powders were prepared by oxides via tumbling ball milling and high-energy ball milling and subsequent carbothermal reduction nitridation.And then X-ray diffractometry(XRD) was adopted to analyze the phase composition of the milled mixtures or composite powders.The results show that the phase evolution sequences of TiO2 followed in the reaction process are:TiO2→Ti3O5→Ti(ON)→Ti(C,N) for tumbling ball milling.But the diffraction peaks of the milled mixtures become wider and the reaction activation of powders are improved by high-energy ball milling,especially without solvent.For the high-energy milled mixtures,Ti(ON) phase does not occur during reaction synthesis and the composite powders of(Ti,15W,5Mo,0.2V)(CN)-20Ni without impurity phase are synthesized at only 1200℃.In every ball milling mode,many W,Mo and V atoms precipitate from Ni solid solution with the formation of Ti(CN) and subsequently dissolve into Ti(CN) structure to form(Ti,W,Mo,V)(CN) solid solution.