Study of NiO/YSZ Anode for SOFC Prepared by Tape Casting

LE Shi-ru,SUN Ke-ning,XU Feng,AN Mao-zhong,ZHANG Nai-qing,ZHU Xiao-dong,FU Qiang

DOI: https://doi.org/10.3321/j.issn:1001-9731.2008.04.027

2008-01-01

Abstract:NiO-μm and NiO-nm in SOFC anodes,which were prepared by tape casting,were compared.It was found that,the maximum power density of the cell with NiO-nm as anode was 257.1mW/cm2 at 800℃,but that was only 124.9mW/cm2 for NiO-μm.The reason was that the anode with NiO-nm has larger trible phase boundary.After calcining at 700℃ for NiO-nm,the power density increased to 369.0mW/cm2,while it deceased to 169.5 and 159.0mW/cm2 at 800 and 900℃ respectively,because NiO calcined at 700℃ improved its activity and held its small particle size,but the particle increased abruptly up to 1.35μm at 800 and 900℃.When YSZ in the anodes calcined at 1200℃,the particle size increased from 0.2-34μm,the maximum power density of the cell decreased to 120.0mW/cm2,because NiO was isolated by large YSZ.However,these YSZ were milled for 12h,the particle size decreased to 0.70μm and the power density increased to 447.9mW/cm2 because of YSZ and NiO distributed uniformity.