Abstract:Atmospheric plasma spraying (APS) was employed to deposit yttria-stabilized zirconia (YSZ) electrolyte for cermet supported tubular solid oxide fuel cells (SOFCs) to reduce manufacturing cost. A post-spray densification process was conducted for the APS-sprayed YSZ coating in order to achieve a required coating density for gas tightness and improved electrical conductivity. The deposition of the YSZ layer was carried out at ambient atmosphere using commercial ZrO2–8 wt.% Y2O3 powder. The densification of the YSZ coating was attained through impregnating yttrium and zirconium nitrate solutions into the porous coating, followed by thermal decomposition of nitrates within the pores of the coating through annealing treatment. The effects of impregnation number on gas permeability and electrical conductivity of the YSZ electrolyte have been examined. It was found that the gas permeability of the YSZ electrolyte layer after the densification treatment reaches a level of 2×10−7 cm4 gf−1 s−1, which is a necessary value for practical operation of SOFCs. The test cell yielded an open circuit voltage of 1.0 V at 930 °C. Furthermore, the anisotropy of the electrical conductivity of the YSZ coating is clearly elucidated by comparing the present result to the reported data. The electrical conductivity of the as-sprayed YSZ coating showed a value of 0.53 S m−1 from the through-thickness direction at 900 °C. The post-densification treatment using nitrate solution improved the electrical conductivity of the YSZ layer by ∼30%.

Effect of Composition of NiO/YSZ Anode on the Polarization Characteristics of SOFC Fabricated by Atmospheric Plasma Spraying

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

Effect of Anode Microstructure on Performance of SOFC Fabricated by Thermal Spraying

Study on Microstructure and Electrochemical Performance of Ni/YSZ Anode Deposited by APS

Influence of YSZ Electrolyte Thickness on the Characteristics of Plasma-Sprayed Cermet Supported Tubular SOFC

Performance of Tubular Solid Oxide Fuel Cell Assembled with Plasma-Sprayed Sc2O3–ZrO2 Electrolyte

Influence of Atmospheric Plasma-Sprayed Composite Cathode on the Performance of Solid Oxide Fuel Cells

Effect of Low Plasma Spraying Power on Anode Microstructure and Performance for Metal-Supported Solid Oxide Fuel Cells

Development of a Ni/Al 2 O 3 Cermet-Supported Tubular Solid Oxide Fuel Cell Assembled with Different Functional Layers by Atmospheric Plasma-Spraying

Influence of Characteristics of Stabilized Zirconia Electrolyte on Performance of Cermet Supported Tubular SOFCs

Development of NiO-GDC Anode by Atmospheric Plasma Spraying for Metal-Supported SOFCs

The Characteristics of Cermet-Supported Tubular Solid Oxide Fuel Cells Manufactured by Thermal Spraying

Performance of YSZ Electrolyte Layer Deposited by Atmospheric Plasma Spraying for Cermet-Supported Tubular SOFC

Reactive Sputtered NiO-YSZ Anode Functional Layer for Thin Film Low-Temperature Solid Oxide Fuel Cell

Microstructure and Electrochemical Behavior of a Structured Electrolyte/LSM-Cathode Interface Modified by Flame Spraying for Solid Oxide Fuel Cell Application

Novel Co-precipitation method to synthesize NiO-YSZ nanocomposite powder for solid oxide fuel cell

The effect of nickel oxide microstructure on the performance of Ni–YSZ anode-supported SOFCs

Thin Yttria-Stabilized Zirconia Electrolyte and Transition Layers Fabricated by Particle Suspension Spray

Effect of Preparation Methods on the Properties of Ni-Ysz Cermets for Sofc Anodes

Effect of densification processes on the properties of plasma-sprayed YSZ electrolyte coatings for solid oxide fuel cells

Fabrication and Property of SOFC via Colloidal Spray Coating