A Comparison of La0.75Sr0.25Cr0.5Mn0.5O3−δ and Ni Impregnated Porous YSZ Anodes Fabricated in Two Different Ways for SOFCs

Xingbao Zhu,Zhe Lue,Bo Wei,Mingliang Liu,Xiqiang Huang,Wenhui Su

DOI: https://doi.org/10.1016/j.electacta.2010.02.028

IF: 6.6

2010-01-01

Electrochimica Acta

Abstract:In this paper, La0.75Sr0.25Cr0.5Mn0.5O3−δ (LSCrM) and Ni impregnated porous yttria-stabilized zirconia (YSZ) anodes have been fabricated in two different ways. The testing results demonstrated the excellent performance of the anode made by infiltrating a mixture of LSCrM and Ni(NO3)2 solutions into porous YSZ matrix. After reduction of the anode with hydrogen, an inner nano-network structure with mixed ionic-electronic conducting path has been formed within and between these added particles. A single cell with the anode at 800°C exhibited the maximum power densities of 1151 and 704mWcm−2 when dry H2 and CH4 were used as the fuels, respectively; under the same conditions, the cell performances for LSCrM and Ni impregnated YSZ anode separately were 810 and 508mWcm−2. A cavity model was proposed to simulate the impregnating process and the loading was calculated. No carbon deposition was detected in the anode, even with the presence of Ni, after operation in dry CH4 for about 6h under open-circuit condition.