Effect of solid solution heat treatment following age hardening on microstructure and mechanical properties of 7000 series power aluminum alloy
Hao Chen,Zhi Wang,Xiaojing Xu,Tabie Vitus,Ze Jiang,Qiang Mao,Hao Wang,Qingjun Liu,Xu Zhang,Yangguang Liu,Yishui Xiao
DOI: https://doi.org/10.1088/2053-1591/ab6775
IF: 2.025
2020-01-22
Materials Research Express
Abstract:In this paper, Al-11.1Zn-2.7Mg-1.7Cu-1.4Ti-0.2Zr alloy material was prepared by powder metallurgy to study the effect of the different solid-solution aging systems on the microstructure and mechanical properties of this 7000 series aluminum alloy. The microstructure of the alloy under the three different solid-solution processes S1, S2, and S3 were observed using an optical microscope, scanning electron microscope, and x-ray diffraction analysis. The mechanical properties were tested to determine the best solid-solution process. The results show that under the S2 solid-solution process, the alloy has the best mechanical properties, with a compressive strength of 646.7(±6.5) MPa and a fracture strain of 5.9(±0.06)%. The maximum hardness trends in the three solid-solution processes after aging are S2 > S3 > S1. The maximum hardness 220.7(±5.5)HV occurs after S2 solid-solution and 121 °C × 18 h aging. Moreover, after S2 solid-solution treatment, the solid-solution degree is close to saturation, the solid-solution strengthening effect is the best, and dislocations contribute the most to the strength.
materials science, multidisciplinary