Abstract:Currently, the hot forming of aluminum alloys has garnered significant attention for overcoming poor formability at room temperature (RT). However, the current hot forming technique is facing problems such as time-consuming procedures and high economic cost. To improve forming efficiency, we herein propose a novel forming technique for heat-treatable aluminum alloys, termed pre-aged hardening warm forming (PHF) process. An Al–Zn–Mg–Cu alloy is used to investigate the flow behavior, drawing formability, and post-forming mechanical properties during the aforementioned process. Uniaxial tensile tests and Erichsen tests are conducted to evaluate the plastic flow behavior and drawability, respectively. Stamping tests are performed on a cap beam component to verify the engineering feasibility of the forming technique. Optical microscopy (OM) and transmission electron microscopy (TEM) are performed to characterize the microstructure evolution during the PHF process. The tensile test results show that the pre-aged alloys exhibit true fracture elongation similar to the fracture elongation of the O-temper alloy at RT, and that the Erichsen values of the pre-aged alloys are 5%–16% higher than that of the O-temper alloy at 200 °C. The results of the stamping tests for the cap beam component indicate that the optimal final strength of the stamped component achieves σ/σ0.2 = 566 MPa/500 MPa, exceeding the strength of the AA7075-T6 alloy. OM observations show that the stamping process does not significantly affect the grain sizes of the pre-aged alloys. TEM results show that numerous thermostable GPⅡ zones exist in the pre-aged alloys, and that the stamping procedure transforms the GPⅡ zones to dispersed η′ phases and results in the entanglement of numerous dislocations. The dual effects of phase transformation and plastic deformation during the PHF process contribute to the desirable mechanical properties of the stamped components.

Effect of Heat Treatment Conditions on Mechanical Properties and Precipitates in Sheet Metal Hot Stamping of 7075 Aluminum Alloy

Study on High-Temperature Mechanical Properties and Forming Limit Diagram of 7075 Aluminum Alloy Sheet in Hot Stamping

Investigation on effect of high-efficiency solid solution and hot stamping process on microstructure evolution and mechanical properties of high-strength aluminum alloy

Experimental and Numerical Investigation on Strengthening Behavior of 7075 Aluminum Alloy Sheets in Hot Forming–Quenching Integrated Process

Precipitates evolution of the AA7075-H18 alloy sheet during the application of the solution heat treatment process

The Effect of Hot Forming–Quenching and Heat Treatment Processes on the Mechanical Properties of AA6016 Aluminum Alloy Sheets

Effect of solution treatment time on plasticity and ductile fracture of 7075 aluminum alloy sheet in hot stamping process

Effect of Thermo-Mechanically Activated Precipitation on the Hot Deformation Behavior of High Strength Aluminum Alloy AA7075

Effect of Solution Heat Treatment on the Microstructure and Microhardness of 7050 Aluminum Alloy

Investigation on strengthening of 7075 aluminum alloy sheet in a new hot stamping process with pre-cooling

The effects of heat treatment on the extrusion-induced inhomogeneity of spray-formed aluminum alloy 7055

Microstructure and Properties Evolution of 7075 Al alloy in Hot Rolling and Short Process Heat Treatment

Effect of heat treatment and extrusion processing on the microstructure and mechanical properties of spray formed 7055 alloy

Investigation of formability, microstructures and post-forming mechanical properties of heat-treatable aluminum alloys subjected to pre-aged hardening warm forming

Investigation on Contact Heating of Aluminum Alloy Sheets in Hot Stamping Process

Effects of heat treatment on a novel continuous casting direct rolling 6056 aluminum alloy: cold rolling characteristics and tensile fracture properties

Effect of heat treatment on some mechanical properties of 7075 aluminium alloy

Deformation Behavior and Mechanical Properties of AA7075 During Pre-hardened Aluminum Alloy Hot Forming Process

Deep drawing of aluminum alloy 7075 using hot stamping

Effect of recrystallization annealing, solid solution and pre-aging intermediate treatment on microstructure and mechanical properties of Al-Mg-Si rolled sheet

Effect of thermomechanical processing on mechanical properties and microstructural evolution of Al-Mg-Zn alloy