On Line Process Technology Research of 7003-T6 Aluminum Alloy Profile

HUANG Zhi-qi,YIN Zhi-min,CHEN Hui,ZHOU Xiang,LIU Zhi-ming,LI Shen-lan
DOI: https://doi.org/10.3969/j.issn.1007-7235.2012.02.009
2012-01-01
Abstract:At laboratory condition the solution process technology of 7003 alloy has been researched,then quenched and two-step aged;the tensile strength,yield strength and elongation of 7003 alloy with T6 temper can get to 405 N/mm2,351 N/mm2 and 13% respectively.Based on this researching,the influence of on line quenching technology,holding time in air and aging process on mechanical properties has been investigated.The tensile strength,yield strength and elongation of 7003-T6 can get to 407 MPa,353 MPa,15.5%,while after on line quenching it being hold in air for 15 days and two-step aged,but the mechanical properties will be 390 N/mm2,353 N/mm2,15.8% respectively if it being single step aged.