Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Effect of multi-stage solution and aging process on microstructure and properties of Al–10.7Zn–2.8Mg–1.2Cu–0.2Zr aluminum alloy extrusion materials

Effect of multi-stage solution on microstructure and properties of Al–10.5Zn–2.05Mg–1.02Cu–0.2Zr–0.923Ti alloy extrusion

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Extruded Al–4Cu–1Li–0.4Mg–0.4Ag–0.18Zr Alloy

Effect of solid solution heat treatment following age hardening on microstructure and mechanical properties of 7000 series power aluminum alloy

Effect of Solid Solution System on the Properties of Al-6.5Si-5.5Cu-0.2Zr-0.01Sr-0.06Ti-0.2Ce Alloy in the Aging State

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Microstructures and Mechanical Properties of Al-Zn-Mg-Cu Alloys under Multi-Directional Severe Strain and Aging

Effect of solution and aging system on microstructure and mechanical properties of 7000 series aluminum alloy produced by powder metallurgy

Microstructure characteristics of an ultra-high strength extruded Al-4.7Cu–1Li-0.5Mg-0.1Zr–1Zn alloy during heat treatment

Effect of the Solid Solution and Aging Treatment on the Mechanical Properties and Microstructure of a Novel Al-Mg-Si Alloy

Effect of Aging Treatment on High Temperature Mechanical Properties of a Cast Al–Li–Cu Alloy

Effect of Zn/Mg ratio on the microstructure and properties of Al-xZn-2.0Mg-1.0Cu-0.2Zr-yTi ultrahigh-strength aluminum alloy extrusion

Influence of isothermal and non-isothermal aging treatments on microstructure and properties of Al-Zn-Mg alloy helical profile

Effect of heat treatments on microstructure and mechanical properties of sand cast Al–2Li–2Cu–0.5Mg–0.2Sc–0.2Zr alloy

Effect of Aging Treatment on Microstructure and Mechanical Properties of As-Extruded AA6063 Aluminum Alloy

Aging precipitation characteristics and tensile properties of Al–Zn–Mg–Cu alloys with different additional Zn contents

Achieving High Performance by Optimized Heat Treatment in a Spray Formed Al–Zn–Mg–Cu Alloy

Effect of Aging Treatment Temperature on Microstructure and Properties of Al-9.3Si-0.41Mg-0.2Zr-0.01Sr-0.08Ti-0.2Ce Cast Aluminum Alloy

Characterization of Hot Extrusion and Heat Treatment on Mechanical Properties in a Spray Formed Ultra-High Strength Al-Zn-Mg-Cu Alloy

Effect of Zn/Mg ratio on T6 state microstructure and properties of Al-xZn-2.6Mg-0.94Cu-0.2Zr-0.8Ti cold extruded aluminum alloy

Microstructural Characteristics and Mechanical Properties of Extruded Al-4Cu-1Li-0.4Mg-0.1Zr-xZn Alloy