Effects of aging on precipitation behavior and mechanical properties of a tensile deformed Al–Cu alloy
Xu-Hao Zhu,Y.C. Lin,Qiao Wu,Yu-Qiang Jiang
DOI: https://doi.org/10.1016/j.jallcom.2020.155975
IF: 6.2
2020-11-01
Journal of Alloys and Compounds
Abstract:<p>A three-stage process, i.e., solution treatment, pre-tensile deformation at intermediate temperatures and aging treatment, is designed to optimize the microstructures and improve the mechanical properties of an Al–Cu alloy. The interactions between the aging temperature (<em>T</em>), aging time (<em>t</em>), precipitation features and mechanical properties of the pre-tensile deformed Al–Cu alloy are investigated by TEM and DSC analysis. The precipitation of phases is largely influenced by <em>T</em> and <em>t</em>. As <em>T</em> is raised from 408 K to 428 K, the contents of θ′′ phases and G.P. zones decrease, while these of θ′ phases increase. If <em>T</em> is further raised, almost all the G.P. zones and θ′′ phases will transform to θ′ phases. However, θ′ phases easily coarsen at high temperature. So, the yield and ultimate tensile strengths first increase and then decrease. In addition, increasing <em>t</em> can enhance the precipitation process, i.e., G.P. zones→θ′′ phases→θ′ phases, which results in the increased content of θ′ phases. Due to the enhanced pinning effect of θ′ phases on dislocations, the yield strength is improved. Based on the comprehensive analysis, the appropriate <em>T</em> and <em>t</em> for the pre-tensile deformed Al–Cu alloy are about 428 K and 24 h, respectively.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering