Microstructures and Mechanical Properties of 7075 Aluminum Alloy Semi-solid Billet by Hot Rolling

Xiaoping ZHENG,Long JIANG,Jinying SONG,Yaqiang TIAN,Liansheng CHEN

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.13.012

2017-01-01

Abstract:7075 aluminum alloy semi-solid plates were prepared by using hot rolling and semi-solid heat treatment and re-hot rolling process. The microstructures of the plate were observed and mechanical properties were tested. The results show that: after hot rolling of the semi-solid billet, α-Al solid particles of the 7075 aluminum alloy semi-solid microstructure are elongated along RD (rolling direction) and TD (plate width direction) direction, but the change of "liquid phase" is not obvious. The α-Al solid particle has good plastic deformation capacity, and the plastic deformation ability of the "liquid phase" is poor. The final mechanical properties of the semi solid plate are yield strength of 125 MPa, the tensile strength of256 MPa, the elastic modulus of 6250 MPa and the elongation of 5.3％. Tensile fracture type is quasi cleavage fracture. There are secondary cracks and holes in the fracture surface, and inclusion or second-phase particles which would cause crack exists in bottom of the tough nest.