Effect of hot rolling reduction rate on semi-solid microstructure of 7075 aluminum alloy

Wenyuan Gong,Guijie Zhang,Xiaoping Zheng,Yaqiang Tian,Jinying Song,Liansheng Chen

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.10.038

2017-01-01

Abstract:The microstructure evolution of 7075 aluminum alloy semi-solid billet by hot rolling and semi-solid isothermal treatment processing ( short for hot rolling SIMA) under different hot rolling reductions was investigated. The difference of the semi-solid microstructure between RD direction and TD direction was analyzed. And the forming mechanism of the semi-solid microstructure by the hot rolling SIMA processing was discussed. The results show that with the increasing of the hot rolling reduction, the grain uniformization and sphericity and the liquid fraction increase, however, the grain size decreases. But while the hot rolling reduction increases from 60% to 80%, the liquid fraction increases slowly;the liquid area of the TD direction still maintained a uniform distribution and the liquid area of the RD direction cluster obviously. The forming mechanism of the semi-solid microstructure by the hot rolling SIMA processing follows the SIMA theory.