Microstructure and mechanical properties of semi-solid 6061 aluminum alloy plate prepared by hot rolling

Wenyuan Gong,Long Jiang,Xiaoping Zheng,Jinying Song,Yaqiang Tian,Liansheng Chen

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.07.020

2017-01-01

Abstract:Semi-solid rolled 6061 alloy plates were prepared by the process of cold rolling, semi-solid heat treatment and hot rolling.Microstructure of the plates was observed, and their mechanical properties were tested.The relationships between microstructure and mechanical properties were studied.The results show that,during hot rolling of the semi-solid billet of the 6061 aluminum alloy, α-Al solid particles have better plastic deformation ability because the particles can be elongated along the directions of RD and TD.However, the"liquid"areas have lower plastic deformation ability due to a little deformation.The tensile strength and elongation of the hot rolling plate of the 6061 semi-solid billet are 125.38 MPa, 6.43%, respectively.Compared to the hot rolled plate of the 6061 as-cast billet,the tensile strength increases by 14.64% and the elongation decreases by 72.57%.