Abstract:Heavy metals accumulated in slurry of dual alkali flue gas desulfurization (FGD) present a significant catalysis to SO3(2-) oxidation, resulting in a waste of effective components for desulfurization. Na2S was adopted to precipitate heavy metal ions in FGD slurry, and the oxidation rate of SO3(2-) was obtained under different concentrations of heavy metal ions, to reveal the inhibition effect of Na2S on SO3(2-) oxidation catalyzed by heavy metal ions. Mn2+ showed a remarkable catalysis to SO3(-2) oxidation, as the initial oxidation rate of SO3(2-) was tripled to 0.65 mmol/(L x min) by adding 1.0 mmol/L Mn2+ into the slurry. SO3(2-) was catalytically oxidized rapidly with the reaction order 0.169 of Mn2+ within first 60 minutes, so it is of great importance to control the concentration of Mn2+ to inhibit SO3(2-) oxidation. At initial pH value of 6.50-8.50, Na2S removed heavy metal ions effectively from FGD slurry. Higher pH value favored the removal of heavy metal ions. The removal efficiencies of Mn2+, Zn2+, Ni2+ and Cd2+ were 91.0%, 88.1%, 85.5%, and above 99.9% respectively under the conditions of initial pH value 8.50 and Na2S dosage 240.0 mg/L. Mn2+ could be used as an indicator for the concentration of the heavy metal ions in the slurry. As the Mn2+ concentration decreased from 1.0 mmol/L to 5.0 x 10(-3) mmol/L by adding Na2S, the initial oxidation rate of SO3(2-) decreased by 64.6% to 0.23 mmol/(L x min). The desulfurization efficiencies increase 3.8%-5.1% by adding Na2S in a pilot scale setup. It comes to conclusion that heavy metal ions precipitation by adding Na2S with an indicator of Mn2+ to inhibit catalytic oxidation of SO3(2-) is feasible to reduce the consumption of desulfurizer in FGD slurry.

Decomposition Characteristics of Manganese Dithionate in Absorption Solution of Flue Gas Desulfurization and Denitration with Pyrolusite Slurry

The Separation of Manganese Sulfate and Manganese Nitrate in Absorption Solution of Flue Gas Desulfurization and Denitration with Pyrolusite Slurry

The Formation of Manganous Dithionate in the Manganese Oxide Flue Gas Desulfurization

Effect of O2 / SO2 Ratio in the Flue Gas on Manganese Extract Process and Byproduct in the Process of Flue Gas Desulfurization with Pyrolusite Pulp

[Inhibition of Sulfite Oxidation Catalyzed by Heavy Metals in Dual Alkali Flue Gas Desulfurization Slurry].

Thermal and Kinetic Study of Manganese Dithionate from Absorbing or Leaching Solution Via TG/XRD/IC Analysis

Enhanced Recovery of Dithionate from Desulfurization with Pyrolusite System by Manganese Dioxide Anode of Spent Batteries

Manganese leaching in high concentration flue gas desulfurization process with semi-oxidized manganese ore

Oxidation kinetics of dithionate compound in the leaching process of manganese dioxide with manganese dithionate

Removal of manganous dithionate (MnS<sub>2</sub>O<sub>6</sub>) with MnO<sub>2</sub> from the desulfurization manganese slurry

Feasibility of Flue-Gas Desulfurization by Manganese Oxides

Formation Characteristics of Dithionate and Sulfate Ions in the Pyrolusite Leaching Process with SO 2

Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate

Mechanism and influence factors of flue gas desulfurization by symbiotic manganese oxides ore

Kinetics Analysis of Ozonation Process of Recovering Manganese Dioxide from Aqueous Phase in the Presence of Manganese Dithionate

Mechanisms of dry flue-gas desulfurization using natural manganese oxide ores

Study on kinetics of flue gas desulfurization with pyrolusite slurry

In-process control of manganese dithionate in the manganese ore-based wet flue gas desulfurization coupled with efficient manganese leaching

Mass Transfer and Kinetics Study on the Sulfite Forced Oxidation with Manganese Ion Catalyst

Removal of Manganous Dithionate (mns2o6) with MnO2 from the Desulfurization Manganese Slurry

Oxidation of SO2 by O-2 and Its Effects on Dithionate Formation during Pyrolusite Leaching Process with Mixture Gas Containing SO2 and O-2