Experimental Research on Low Temperature Manganese Oxides SCR Denitrification for Oxy-Fuel Combustion Flue Gas

Yamei Li,Yating Wang,Dong Zhao,Ziyi Zhen,X. Gou
Abstract:Nitrogen oxides are one of the major sources of pollution in coal-fired power plants, and they may produce nitrate particles further forming PM2.5, which causes serious damage to human health. In this paper, the denitrification effects of manganese oxides on low-temperature oxy-fuel combustion flue gas were studied based on the different SCR catalysts with different morphology and specific surface area obtained by two different preparation methods of solution combustion synthesis and coprecipitation. The results from experiments show that the denitrification rate of Mn3O4 increases first and then decreases with the increase of temperature under CO2 atmosphere, and it reaches the peak value of 90.2% at 200 ̊C; the denitrification rate of Mn3O4 increases first and then decreases with the increase of temperature under N2 atmosphere, and it reaches the peak value of 93.6% at 200 ̊C. As for Mn3O4/AC catalyst, under CO2 atmosphere, the denitrification rate increases with the increase of temperature and reaches 75% at 300 ̊C; under N2 atmosphere, it increases with the temperature increasing and reaches 78% at 300 ̊C. In CO2 or N2 atmosphere, Mn3O4/AC denitrification rate increases as the oxygen concentration increases and the rate decreases as the SO2 concentration increases.
Engineering,Environmental Science
What problem does this paper attempt to address?