Abstract:We prepare Pd40.5Ni40.5P19 glassy samples with purified ingots by copper mold casting at a high cooling rate and by water quenching at a low cooling rate. Both of them exhibit different supercooled liquid regions and multiple glass transition characteristics in their differential scanning calorimetric curves. The plasticity of the glassy sample prepared by copper mold casting is about 5% while that prepared by water quenching is almost zero (0.2%), indicating that cooling rate has influenced the plasticity of glassy alloys. By using high resolution TEM image analysis, it is revealed that there exist characteristic regions with different contrasts in the full glassy samples. The characteristic size is about 20–40 nm for the glassy sample prepared by water quenching and 2–4 nm for the one prepared by copper mold casting. The large difference in the plasticity of the glassy samples prepared by different cooling rates is believed to be related to the difference in the size of the characteristic nanoscale structures. The results indicate that adjusting cooling rate in preparation of glassy samples could modify the thermal and mechanical properties of the glassy alloys.

Preparation and Thermal Stability of Pd_(77.5)Cu_6Si_(16.5) Bulk Metallic Glass

Preparation and Thermal Stability of Pd 40.5 Ni 40.5 Si X P 19− X Bulk Metallic Glasses

Preparation of a Pd-Cu-Si Bulk Metallic Glass with a Diameter Up to 11 Mm

Formation of Pd-Ni Based Bulk Metallic Glasses

The Effect of Purification on the Glass-Forming Ability of a Pd-Cu-Si Alloy

Investigation of A Ductile and Corrosion-Resistant Pd79au1.5ag3si16.5 Bulk Metallic Glass

Pd-Si Binary Bulk Metallic Glass Prepared at Low Cooling Rate

Glass-forming ability and thermoplastic formability of a Pd 40 Ni 40 Si 4 P 16 glassy alloy

Thermal stability and fragility of Pd–Si binary bulk metallic glasses

Pd-Si binary bulk metallic glass

Structural Stability of Pd40Cu30Ni10P20 Metallic Glass in Supercooled Liquid Region

Influence of Flux Treatment on the Glass Forming Ability of Pd-Si Binary Alloys

Effects Of The Cooling Rate On The Plasticity Of Pd40.5ni40.5p19 Bulk Metallic Glasses

Microstructural Features of Phase Transformation in a Binary Pd–Si Metallic Glass

Effects of the Cooling Rate on the Plasticity of Pd 40.5 Ni 40.5 P 19 Bulk Metallic Glasses

Structural heterogeneity in a binary Pd–Si metallic glass

Glass-forming ability correlated with the liquid-liquid transition in Pd42.5Ni42.5P15 alloy

Cu-alloying Effect on Crystallization Kinetics of Ti41Zr25Be28Fe6 Bulk Metallic Glass

Superductile Bulk Metallic Glass

Preparation of (ti0.45cu0.378zr0.10ni0.072)100−xsnx Bulk Metallic Glasses

Formation and Mechanical Properties of Pd-Si Binary Bulk Metallic Glasses