Abstract:A tri-layer coating of mullite/Y2Si2O7/(70wt%Y2Si2O7+30wt%Y2SiO5) was prepared on carbon fiber reinforced silicon carbide (C/SiC) composite substrate through dip-coating route for the sake of improving oxidation resistance of C/SiC composites. An Al2O3–SiO2 sol with high solid content was selected as raw material for mullite, and a slurry of Y2O3 powder filled silicone resin was used to synthesize yttrium silicate. The microstructure, phase composition, and oxidation resistance of the coating were investigated. The as-fabricated coating shows high density and favorable bonding to C/SiC substrate. After oxidation at 1400 and 1500 °C for 30 min under static air, the flexural strengths of coated C/SiC composite were both increased by ~30%. The desirable thermal stability and the further densification are responsible for excellent oxidation resistance. With the additional help of compatible thermal expansion coefficients among substrate and sub-layers in coating, the coated composite retained 111.2% of original flexural strength after 12 times of thermal shock in air from 1400 °C to room temperature. The carbothermal reaction at 1600 °C between free carbon in C/SiC substrate and rich SiO2 in mullite resulted in severe frothing and desquamation of coating and obvious degradation in oxidation resistance.

Oxidation Protection of C/Si–C–N Composite by a Mullite Interphase

Oxidation protection and behavior of C/C composites with an in situ SiC nanowire-SiC-Si/SiC-Si coating

Oxidation Protection of C/C Composites with a Multilayer Coating of SiC and Si + SiC + SiC Nanowires

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process

Oxidation protection of carbon fibers by a reaction sintered nanostructured SiC coating

Optimum Compositions of Si3N4 -Mosi2/si- SiC Anti-Oxidation Coating for C/C Composites

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Oxidation Protection of C/C Composites by Ultra Long SiC Nanowire-Reinforced SiC–Si Coating

Anti-oxidation performance of mini SiC/SiC composites containing ZrSiO 4 multilayer interphase

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

Cyclic ablation behaviors of mullite‐modified C/C–ZrC–SiC composites prepared by PIP

SiCn/SiC Oxidation Protective Coating for Carbon/carbon Composites

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Mo-Si-C-N Multi-Layer Anti-Oxidation Coating on C/C Composites

SiC Nanowire-Toughened SiC–MoSi2–CrSi2 Oxidation Protective Coating for Carbon/carbon Composites

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

A study on the cycling oxidation behavior of mullite-coated silicon carbide

Toughening by SiC Nanowires in a Dense SiC–Si Ceramic Coating for Oxidation Protection of C/C Composites