Abstract:SiC/h-BN multiphase ceramics were prepared via spark plasma sintering (SPS) with t-BN and SiC nanopowders as raw materials and B2O3 as a sintering additive. The phase composition and microstructure of specimens were characterized by X-ray diffraction and scanning electronic microscopy. The effect of sintering additive content on the sintering behavior, densification, microstructure and mechanical properties of SiC/h-BN multiphase ceramics was investigated. The results show that the addition of B2O3 can effectively increase the density and mechanical properties at a low sintering temperature. Compared to the samples without B2O3 additive, the B2O3 additive is effective to decrease the initial shrinkage temperature, promote the rearrangement of h-BN flake grains and improve the bonding strength between the grains. The density of multiphase ceramics increases, and the mechanical properties firstly increase and then decrease with the increase of sintering additive content. The relative density and mechanical properties of the sample with 5% B2O3 content are better than those of other samples, and the relative density, flexural strength, fracture toughness and elastic modulus are 96.92%, 274.7 MPa, 2.91 MPa·m1/2 and 127.2 GPa, respectively. However, the excessive addition of B2O3 is not conducive to the improvement of mechanical properties.

Pressureless sintering of boron carbide ceramics with Al–Si additives

Pressureless Sintering of Boron Carbide with Al2o3 and Sic As Sintering Aids

Pressureless Sintering of ZrB2–SiC Ceramics: the Effect of B4C Content

Progress in pressureless sintering of boron carbide ceramics – a review

Effects of boron source on properties of pressureless solid-state sintered silicon carbide ceramics

The effect of aluminum additive on pressureless sintering of SiC

High Thermal Conductivity in Pressureless Densified SiC Ceramics with Ultra-Low Contents of Additives Derived from Novel Boron–carbon Sources

Pressureless sintered Al4SiC4 ceramics with Y2O3 addition

Pressureless densification of HfB2-based ceramics using HfB2 powders by borothermal reduction

B4C-SiC composites with tuneable mechanical properties: Role of Al2O3 - Y2O3 sintering additives

Pressureless sintering and ablation behavior of PyC-Csf/ZrB2-SiC-ZrC ceramics doped with B4C

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Influence of Silicon Addition on the Sintering Behavior and Mechanical Properties of Boron Carbide by SPS Process

Effects of silicon addition on the microstructure and properties of B 4 C–SiC composite prepared with polycarbosilane-coated B 4 C powder

Processing and Characterization of SiB0.5C1.5N0.5 Produced by Mechanical Alloying and Subsequent Spark Plasma Sintering

Pseudo low-temperature sintering effect and microstructure evolution of SiBCO ceramics

Effect of the Addition of Carbon on the Sintering Properties of Boron Carbide Ceramics Prepared by Pressureless Sintering

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Pressureless solid-state sintering of SiC ceramics with BN and C additives

Enhanced Mechanical Properties of Nanocrystalline B4C–SiC Composites by In-Situ High Pressure Reactive Sintering