Study on the effects of bilateral laser-assisted cutting on surface integrity and fatigue life of FeCoCrNiAl0.6 alloy

Ping Zhang,Zhenyong Lin,Tengfei Zhang,Changyin Lan,Xiaomin Jiang

DOI: https://doi.org/10.1016/j.engfailanal.2024.108921

IF: 4

2024-10-02

Engineering Failure Analysis

Abstract:This study investigates the impact of various cutting parameters in both unilateral and bilateral laser-assisted cutting processes on the surface integrity and fatigue life of FeCoCrNiAl0.6 high-entropy alloy. By utilizing ABAQUS/FE-SAFE simulations and conducting laser-assisted cutting and fatigue tensile tests, differences in surface quality and fatigue life cycles of FeCoCrNiAl0.6 alloy samples under different cutting scenarios were evaluated. The results indicate that in high-speed laser-assisted cutting, an increase in laser speed leads to a progressive decline in surface quality for both unilateral and bilateral methods. Nevertheless, at a laser speed of 4000 mm/s, optimal surface quality is achieved in both approaches, with the bilateral method consistently providing superior results across varying speeds. Regarding residual stress, unilateral laser-assisted cutting at 4000 mm/s produces a surface residual compressive stress of 532 MPa, which is twice as high as that observed at 10000 mm/s. The bilateral method shows a symmetric distribution of residual compressive stress, with peak values of 567 MPa and 528 MPa on the front and back surfaces, respectively. In terms of fatigue life, bilateral laser-assisted cutting demonstrates enhanced performance at 4000 mm/s, achieving a fatigue life cycle that is 4.72 times longer than that of the unilateral method. Overall, bilateral laser-assisted cutting improves the fatigue life of the material through symmetric thermal effects and higher residual compressive stress, particularly at lower laser speeds and optimal cutting depths.

engineering, mechanical,materials science, characterization & testing