Abstract:This paper presents a comprehensive investigation of the effects of cutting parameters on the surface integrity of milled γ-TiAl alloys. Surface topography, surface roughness, surface defects, plastic deformation, micro-hardness, chip morphology, and tool wear of the milled γ-TiAl alloys were analyzed. The results indicate that the feed rate had the greatest influence on the surface topography and surface roughness. The value of surface roughness increased with the increase in cutting depth and feed rate. However, with the increase in cutting speed, it initially increased and then decreased. The minimum surface roughness was found to be 0.066 μm. The thickness of the plastic deformation layer and the micro-hardness value increased with the increase in cutting depth and feed rate. Also, they initially increased and then decreased with the increase in cutting speed. The minimum thickness of the plastic deformation layer was 15 μm and the depth of the hardened layer on the processed surface varied between 55 and 70 μm. The chip morphology was closely related to the quality of the processed surface. When the cutting depth and feed rate decreased, the chip morphology was transformed from segmented to nearly smooth. When the cutting depth and feed rate reached a critical point, plastic processing of γ-TiAl was achieved. Compared to brittle deformation, a more favorable processed surface was obtained. Finally, the comparison tests of tool wear were carried out with dry and flood coolant cutting. When the cutting speed reached 120 m/min in dry cutting, the tool life was very poor, and the cutting distance was only 1 m. However, the tool life was generally good when cutting with low cutting speed under the following conditions: vc = 60 m/min, ap = 0.1 mm, and fz = 0.01 mm/tooth. Under these conditions, the cutting distance was 60 m in dry cutting with the tool wear of 0.2 mm and 120 m in flood coolant cutting with the tool wear of 0.1 mm. The tool life in flood coolant operation was better than that of dry operation. The tool life decreased to 30 m when cutting with high cutting speed or feed rate (ap = 0.25 mm or fz = 0.025 mm/tooth).

Comparative study on machinability and surface integrity of γ-TiAl alloy in laser assisted milling

Cutting performance and coated tool wear mechanisms in laser-assisted milling K24 nickel-based superalloy

Machining characteristics of Ti6Al4V alloy in laser-assisted machining under minimum quantity lubricant

Enhancing machinability of Ti6Al4V by ultrashort-pulse laser-induced modification assisted grinding

Surface integrity of laser-assisted turning of the GH4169 alloy

Microstructure- and Cooling/lubrication Environment-Dependent Machining Responses in Side Milling of Direct Metal Laser-Sintered and Rolled Ti6Al4V Alloys

Machinability of γ-TiAl: A review

Research on material removal of Ti-6Al-4V by laser-belt machining

Effects of machining surface and laser beam scanning strategy on machinability of selective laser melted Ti6Al4V alloy in milling

The influence of induction-assisted milling on the machining characteristics and surface integrity of γ-TiAl alloys

Microstructural modulation of TiAl alloys for controlling ultra-precision machinability

Numerical Study on Laser-assisted Machining of Ti6Al4V Titanium Alloy

Improved direct laser assisted machining of Al 7075-T6 and Ti-6Al-4V using cubic zirconia tool

Computational investigation on the surface cutting of γ-TiAl alloy

Machinability of c-TiAl: A review

Study of surface integrity of milled gamma titanium aluminide

Feasibility analysis and process characteristics of selective laser ablation assisted milling Inconel 718

Experimental Investigation and Numerical Analysis for Machinability of Alumina Ceramic by Laser-Assisted Grinding

Study on machinability characteristics of novel additive manufactured titanium alloy (Ti-6Al-4V) fabricated by direct metal laser sintering

Tool Wear and Surface Integrity of γ-TiAl Cryogenic Coolant Machining at Various Cutting Speed Levels

Surface micro-texture and tribological properties in longitudinal-torsional ultrasonic-assisted milling Ti2AlNb