Microstructure and Tribological Properties of AlCoCrFeNi2.1 Dual-Phase High-Entropy Alloy Enhanced by Laser Remelting

Yinghui Dong,Bingwen Lu,Zhaobing Cai,Guangpei Lin,Xi Zhou,Bingxu Wang,Chongmei Wang,Le Gu
DOI: https://doi.org/10.1007/s11665-024-10219-w
IF: 2.3
2024-10-09
Journal of Materials Engineering and Performance
Abstract:A number of AlCoCrFeNi 2.1 dual-phase HEA samples were prepared by vacuum induction melting technology, and the surface of the alloy was remelted by laser. The influence of different laser powers on the microstructure and tribological properties of the AlCoCrFeNi 2.1 dual-phase HEA was studied by changing the laser power in the remelting process. Laser remelting technology has no effect on the dual-phase structure (FCC, BCC) of AlCoCrFeNi 2.1 dual-phase HEA, but changes the ratio and grain size. After laser remelting, the microhardness of AlCoCrFeNi 2.1 dual-phase HEA will increase. When the laser power is 1400 W, its microhardness reaches the maximum (339.28 ± 2.98 HV), which is 1.3 times that of AlCoCrFeNi 2.1 dual-phase HEA before remelting. However, with the continuous increase in laser power, the microhardness of AlCoCrFeNi 2.1 dual-phase HEA will increase. The microhardness of AlCoCrFeNi 2.1 dual-phase HEA was slightly reduced. Similar to the wear rate of microhardness, the wear rate of AlCoCrFeNi 2.1 dual-phase HEA first increases and then decreases with the increase in laser power. This phenomenon is due to the fact that too high laser power will speed up the cooling rate and lead to defects in the cladding layer. However, the wear mechanism of AlCoCrFeNi 2.1 dual-phase HEA after remelting with different laser powers is the same, including oxidation wear, adhesion wear and fatigue wear.
materials science, multidisciplinary
What problem does this paper attempt to address?