Microstructure evolution and mechanical properties of Al CoCrFeNi high-entropy alloys by laser melting deposition

Liufei Huang,Yaoning Sun,Abdukadir Amar,Changgui Wu,Xue Liu,Guomin Le,Xiaoying Wang,Jian Wu,Kun Li,Chunli Jiang,Jinfeng Li
DOI: https://doi.org/10.1016/j.vacuum.2020.109875
IF: 4
2021-01-01
Vacuum
Abstract:<p>Al<sub><em>x</em></sub>CoCrFeNi (<em>x</em> = 0, 0.2, 0.45, 0.7 and 1) high entropy alloys (HEAs) have been successfully synthesized by laser melting deposition (LMD). It is found that the microstructure of LMD-CoCrFeNi HEA with increasing the content of Al has been transformed from a single face-centered cubic (FCC) phase to mixture of FCC + BCC duplex phases, and then to body-centered cubic (BCC/B2) phases. The addition of Al (Al<sub>0.2</sub>, Al<sub>0.45</sub> and Al<sub>0.7</sub>) remarkably improved the yield strength σ<sub>0.2</sub> (from 138 MPa to 185 MPa, 262 MPa and 771 MPa) and the tensile strength σ<sub>t</sub> (from 634 MPa to 675 MPa, 863 MPa and 1171 MPa) of the samples, with the prize of plasticity decrease from 46% to 45%, 41% and 11% in tension. This work provides an approach of LMD-fabricated CoCrFeNi-based HEAs with different Al addition to accommodate the microstructure and mechanical properties, and insights into the correlation of mechanical properties with the solid solution strengthening or/and the precipitation of hardening phase.</p>
materials science, multidisciplinary,physics, applied
What problem does this paper attempt to address?
This paper aims to explore the microstructural evolution and mechanical properties of AlxCoCrFeNi high - entropy alloys (HEAs) prepared by laser melting deposition (LMD) technology. Specifically, the study focuses on how the change in aluminum (Al) content affects the microstructure and mechanical properties of these alloys. As the aluminum content increases, the microstructure of the alloy changes from a single face - centered cubic (FCC) phase to an FCC + BCC two - phase mixture, and finally to a body - centered cubic (BCC/B2) phase. In addition, the paper also discusses the effect of adding aluminum on the yield strength (\(\sigma_{0.2}\)) and tensile strength (\(\sigma_t\)) of the alloy, as well as the strengthening mechanisms behind this change, such as solid - solution strengthening or precipitation of hardening phases. It is found that as the aluminum content increases, the yield strength and tensile strength of the alloy are significantly improved, but the plasticity is somewhat decreased. This provides a new method for manufacturing CoCrFeNi - based high - entropy alloys with different aluminum contents by LMD technology, and helps to understand the relationship between the mechanical properties and microstructure of these alloys.