Abstract:Abstract Additive manufacturing (AM) is a developing manufacturing technology, which provides excellent attributes compared to other manufacturing techniques. However, one of the critical challenges is the presence of defects that hinder the mechanical properties of the parts, particularly the fatigue life. Experimental understanding of fatigue is a cumbersome process. Therefore, numerical prediction based on specified conditions (such as porosity and applied load) can be an alternative to experimental analysis at the design stage of AM parts. In this study, elastic–plastic finite element analysis (FEA) is performed to obtain the stress distribution around pores, and their resultant effect on fatigue life for L-PBF (laser powder bed fusion) produced AlSi10Mg alloy samples. The stress field is calculated for both single and multiple pore models, where stress concentration is evaluated as a function of the pore’s location and its size. It is found that both pore location and size affect the stress field; however, location effects dominate over pore size. For the same remote applied stress level, the stress concentration around the pore increases with an increase in pore size, and the local maximum stress occurs near the pores that are closest to the surface. The current study also evaluates the relative effect of porosity fraction, average pore size, and location. It is found that the magnitude and sensitivity of stress concentration are hierarchically controlled by porosity location, pore size, and porosity density. A multi-scale finite element (FE) model is proposed based on inherent porosity data measured using Computed Tomography (CT) to predict overall fatigue life. The fatigue cycles are calculated using the rainflow counting algorithm in FE Safe using the stress–strain data obtained from the proposed FEA model. Using the proposed model, it is possible to generate S–N curves for any loading condition for a given porosity condition (porosity density and average pore size). The S–N curve results obtained from the FE model are compared to the experimental observations. The predicted fatigue life shows approximately 5% error with experimental results at high stress loading conditions. However, the proposed model overpredicts the fatigue life at low stress loading by almost 30%.

Fatigue behavior under variable amplitude loadings in AlSi10Mg alloy components produced by laser powder bed fusion

Failure analysis of fatigue crack propagation in specimens of AlSi10Mg aluminum alloy produced by L-PBF: Effect of different heat treatments

Fatigue crack nucleation and growth in laser powder bed fusion AlSi10Mg under as built and post-treated conditions

Hot dwell-fatigue behaviour of additively manufactured AlSi10Mg alloy: Relaxation, cyclic softening and fracture mechanisms

Fatigue characteristics of a newly developed laser powder bed fused scandium-free Al-Mg-Zr-Mn alloy

Fatigue life prediction of additively manufactured AlSi10Mg based on surface roughness and residual stress

Defect sensitivity in L-PBF AlSi7Mg0.6 alloy subjected to fatigue load: Effect of load ratio and torsion loading

Effect of heat treatment on fatigue crack growth performance of AlSi10Mg aluminum alloy submitted to LPBF

High Cycle Fatigue Property of Al–Mg–Sc–Zr Alloy Fabricated by Laser Powder Bed Fusion

Residual Stress and Long Fatigue Crack Growth Behaviour of Laser Powder Bed Fused Ti6Al4V: Role of Build Direction

High-cycle-fatigue Properties of Selective-Laser-melted AlSi10Mg with Multiple Building Directions

The effect of defect population on the anisotropic fatigue resistance of AlSi10Mg alloy fabricated by laser powder bed fusion

Novel method of residual stress reduction for AlSi10Mg manufactured using selective laser melting without compromise of mechanical strength

On the effect of loading and printing parameters that influence the fatigue behavior of laser powder-bed fusion additively manufactured steels

Mechanical Properties of AlSi10Mg Processed by Laser Powder Bed Fusion at Elevated Temperature

Microstructure, mechanical properties and fatigue crack growth behavior of an Al-Zn-Mg-Cu-Si-Zr-Er alloy fabricated by laser powder bed fusion

Low cycle fatigue response and fracture mechanism in a novel Al-3.5Si-0.5Mg-0.4Cu casting alloy

Very-high-cycle fatigue behavior of AlSi10Mg manufactured by selected laser melting: Crystal plasticity modeling

Effect of Post-Processing Treatment on Fatigue Performance of Ti6Al4V Alloy Manufactured by Laser Powder Bed Fusion

High Cycle Fatigue Performance of AlSi10mg Alloy Produced by Selective Laser Melting

Analysing the effect of defects on stress concentration and fatigue life of L-PBF AlSi10Mg alloy using finite element modelling