Abstract:The steel-concrete interface (SCI) is known to play a major role in corrosion of steel in concrete, but a fundamental understanding is still lacking. One reason is that concrete's opacity complicates the study of internal processes. Here, we report on the application of bimodal X-ray and neutron microtomography as in-situ imaging techniques to elucidate the mechanism of steel corrosion in concrete. The study demonstrates that the segmentation of the specimen components of relevance - steel, cementitious matrix, aggregates, voids, corrosion products - obtained through bimodal X-ray and neutron imaging is more reliable than that based on the results of each of the two techniques separately. Further, we suggest the combination of tomographic in-situ imaging with ex-situ SEM analysis of targeted sections, selected on the basis of the segmented tomograms. These in-situ and ex-situ characterization techniques were applied to study localized corrosion in a very early stage, on reinforced concrete cores retrieved from a concrete bridge. A number of interesting observations were made. First, the acquired images revealed the formation of several corrosion sites close to each other. Second, the morphology of the corrosion pits was relatively shallow. Finally, only about half of the total 31 corrosion initiation spots were in close proximity to interfacial macroscopic air voids, and above 90 percent of the more than 160 interfacial macroscopic air voids were free from corrosion. The findings have implications for the mechanistic understanding of corrosion of steel in concrete and suggest that multimodal in-situ imaging is a valuable technique for further related studies.

Iron-oxide-identifying imaging method based on a wide-energy neutron beam for corrosion inspection in reinforced concrete structures

Improved Magnetic-Based Apparatus Enables Non-Destructive and High Sensitive Steel-Bar Corrosion Detection

Corrosion Damages of Reinforced Concrete Characterized by X-ray CT and DVC Techniques

Nondestructive Corrosion Detection in RC Through Integrated Heat Induction and IR Thermography

Magnetic resonance eddy penetrating imaging for detecting reinforcement corrosion in concrete

THE CORROSION MONITORING USING RESISTANCE-PROBE METHOD IN THE CEMENT MOTAR AND COMPARING WITH ELECTROCHEMISTRY-PROBE METHOD

Non-uniform Corrosion of Steel in Mortar Induced by Impressed Current Method: an Experimental and Numerical Investigation

Chloride-induced corrosion of steel in concrete -- insights from bimodal neutron and X-ray microtomography combined with ex-situ microscopy

Critical thickness of rust layer at inner and out surface cracking of concrete cover in reinforced concrete structures

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Mill Scale and Corrosion Layer at Concrete Surface Cracking

Corrosion damage detection in reinforced concrete using Rayleigh wave-based method

THE STATE OF THE ART OF CONCRETE STRUCTURE DURABILITY MONITORING AND RESTORATION

An Optical Fiber Sensor Method for Simultaneously Monitoring Corrosion and Structural Strain Induced by Loading

Combined Application of Novel Electromagnetic Sensors and Acoustic Emission Apparatus to Monitor Corrosion Process of Reinforced Bars in Concrete

Nondestructive evaluation of rebar corrosion in concrete structures using ultrasonics and laser-based sensing

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Composition and expansion coefficient of rust based on X-ray diffraction and thermal analysis

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Electrical impedance spectroscopy-based nondestructive testing for imaging defects in concrete structures

Experimental Research on Corrosion-Induced Cracking Monitoring Based on Optical Fiber Sensor