Abstract:Here, it is demonstrated that Fe‐foil/Mg3(Sb, Bi)2 interface sintered at 1073 K effectively prevented a significant diffusion and realized the dual purpose of realizing both the material's high performance and low interfacial resistance. Coupled with p‐type Bi2Te3, a high‐performance thermoelectric module is fabricated showing a competitive efficiency of 7.1% at the hot‐side temperature of 523 K. Mg3(Sb, Bi)2‐based materials possess excellent room‐temperature thermoelectric performance, while poor interfacial behaviors occur when connected with metal electrodes due to the strong chemical activity and volatility of Mg element. In this study, a high efficiency of 7.1% under a temperature difference of 230 K is achieved in n‐Mg3(Sb, Bi)2/p‐Bi2Te3 thermoelectric module. When changing the interfacial layer from Fe powder to Fe foil, it effectively prevents a significant diffusion of both Mg and Bi elements from the material matrix to the interfacial layer, resulting in an extremely low contact resistivity ≈3.4 μΩ cm2 that is almost one order lower than of that of Fe powder/Mg3(Sb, Bi)2 junction ≈30 μΩ cm2. Particularly, a thin diffusion layer with a width of ≈2 μm is initially observed in the unannealed Fe foil/Mg3(Sb, Bi)2 junction. Even after thermal aging at 573 K for 28 days, the diffusion‐layer width is basically unchanged and its corresponding contact resistivity maintained as low as ≈5.8 μΩ cm2. Overall, this work provides deep insights into interfacial design and paves the way for high‐performance and sustainable low‐grade waste heat recovery.

Interfacial Stability in Bi2Te3 Thermoelectric Joints

Enhanced Contact Performance and Thermal Tolerance of Ni/Bi2Te3 Joints for Bi2Te3-Based Thermoelectric Devices

Interfacial Reactions in the Sn-Bi/Te Couples

Interface Microstructure and Performance of Sb Contacts in Bismuth Telluride-Based Thermoelectric Elements

Ni barrier in Bi2Te3-based thermoelectric modules for reduced contact resistance and enhanced power generation properties

Enhanced Interfacial Reliability and Mechanical Strength of CoSb3-Based Thermoelectric Joints with Rationally Designed Diffusion Barrier Materials of Ti-Based Alloys

Ni–W–P layer-induced strength improvement of solder joint in Bi2Te3 thermoelectric module

Interfacial Reactions in Thermoelectric Modules

Effect of NiMo Diffusion Barrier Plating Preparation on Microstructure and Properties of Bi2Te3/Cu Joints

Enhancing Interfacial Stability and Mechanical Strength of a CoSb3-Based Thermoelectric Junction Using Ti-Based Alloy Barrier Layers.

Polarity Effect in a Sn3Ag0.5Cu/Bismuth Telluride Thermoelectric System

Microstructural evolution and failure mechanism dominated by Bi, Sb cooperative diffusion at p-type thermoelectric pillar Bi-Sb-Te/Sn interface

Co/Bi2te3 Interfacial Reactions and Bi-Co-Te Phase Equilibria

Enhancing the Thermoelectric Property of Bi2Te3 Through a Facile Design of Interfacial Phonon Scattering

Thermoelectric Performance of Sb2Te3-Based Alloys is Improved by Introducing PN Junctions.

Interfacial Design Contributing to High Conversion Efficiency in Mg3(Sb, Bi)2/Bi2Te3 Thermoelectric Module with Superior Stability

Interfacial Reactions between Sn-Based Solders and n-Type Bi2(Te,Se)3 Thermoelectric Material

EFFECT OF OPERATING TEMPERATURE ON INTERFACE DIFFUSION AND POWER GENERATION OF BISMUTH TELLURIDE THERMOELECTRIC MODULES

Effect of Interfacial Compound Formation on Contact Resistivity of Soldered Junctions Between Bismuth Telluride-Based Thermoelements and Copper

Interfacial reactions at the joints of PbTe thermoelectric modules using Ag-Ge braze

Improved contact performance and thermal stability of Co–Ni alloy barrier layer for bismuth telluride-based thermoelectric devices