Abstract:High-strength ceramics were prepared from high alumina fly ash (HAFA) and activated alumina as raw materials with magnesia as a sintering additive. The growth kinetics and influence mechanism of secondary mullite whiskers were investigated. Meanwhile, the effects of the Al2O3/SiO2 mass ratio (A/S) and the amount of magnesia on the content and morphology of mullite in the green body were investigated, so as to emphasize the effect of the liquid phase in the sintering process on the growth of secondary mullite whiskers. The results showed that the aspect ratio of secondary mullite whiskers increased significantly after adding activated alumina to increase the A/S ratio of raw materials. When 30 wt% activated alumina was added, the mullite content increased by 5.39%, and the whisker length increased from 1.36 μm to 4.18 μm. The addition of magnesia improved the liquid phase formed during the sintering process and the K value method was used to determine the sintering liquid phase content under various conditions. It was observed that increasing the magnesia level by 1 wt% could raise the liquid phase content by 5–7%. When the total liquid content of the system was 30–40%, the growth activation energy in the diameter direction of the whisker reduced significantly, promoting the growth of secondary mullite whiskers along the C axis. The morphology of mullite gradually developed from fibrous to long columnar crystal, making it combine more densely with the green body matrix. Furthermore, the staggered long columnar mullite crystal structure changes the fracture mode of ceramics from intergranular to transgranular fracture, which fully uses the high mechanical strength of mullite. As a result, the fracture energy and strength of ceramics are significantly improved.

An engineering ceramic-used high-temperature-resistant inorganic phosphate-based adhesive self-reinforced by in-situ growth of mullite whiskers

Multiple high-temperature resistant phases modified phosphate-based adhesive for engineering ceramic connection in extreme environment

A Composite Structural High-Temperature-resistant Adhesive Based on In-Situ Grown Mullite Whiskers

Low-temperature in-situ grown mullite whiskers toughened heat-resistant inorganic adhesive

The effect of multiple factors on the synthesis of mullite whiskers based on the S-L-S mechanism and the comparison of strengthening performance

The preparation of mullite foamed ceramics reinforced by in-situ SiC whiskers and their reinforcement mechanism

A ceramizable adhesive with high temperature resistance at 1400°C: Bonding strength and bonding mechanism

Properties and mechanism of mullite whisker toughened ceramics

In situ mullite whisker network formation for high strength and lightweight ceramic proppants

Mechanical properties of reinforced porcelain slabs with mullite whiskers introduced by aluminum silicate fiber

Preparation of mullite whiskers from high alumina fly ash and its reinforced porous structure

Analysis of Factors Affecting the Preparation of Mullite Whiskers from Silica-Rich Slag and Application Studies

Mechanical and Thermal Properties of Phosphoric Acid Activated Geopolymer Materials Reinforced with Mullite Fibers

Cost-effective Utilization of Mineral-Based Raw Materials for Preparation of Porous Mullite Ceramic Membranes Via In-Situ Reaction Method

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

The preparation and properties of an alloying modified ceramic-precursor high-temperature resistant adhesive for joining zirconia ceramics and titanium-based superalloys

Microstructure and Properties of Porous Anorthite/mullite Whiskers Ceramics with High Porosity

Mullite Whisker Reinforced Porous Anorthite Ceramics with Low Thermal Conductivity and High Strength

SPS Fabrication of Whisker and ZrO2 Co-toughened Mullite Ceramics

Near‐net‐size Preparation of Porous Mullite Matrix Ceramics with in Situ Formed 3D Mullite Whisker Network

Seed assisted in-situ synthesis of porous anorthite/mullite whisker ceramics by foam-freeze casting