Multiple high-temperature resistant phases modified phosphate-based adhesive for engineering ceramic connection in extreme environment

Mingchao Wang,Qinggong Song,Yuqing Gu,Chongrui Wu,Jiachen Liu,Xiaomeng Zhou,Mingrun Du

DOI: https://doi.org/10.1016/j.ceramint.2018.09.203

IF: 5.532

2019-01-01

Ceramics International

Abstract:The lower-strength defect of inorganic phosphate adhesive had been definitely improved by self-generating multiple high-temperature resistant phases. Compared to our previous product, the best bonding performance of this novel adhesive for mullite was increased by 270%, which was close to some popular preceramic polymer-based adhesives. The apparent shear strength at room temperature was up to 33.1 MPa after calcination at 900 °C, while the high-temperature strength researched 23.3 MPa at 900 °C and maintained above 17 MPa from 700° to 1200 °C. The reinforced effect of adhesive owed to the introduction of various Cu-based intermetallics, the premature generation of Al4B2O18 at 900 °C, and the structure optimizing through the oxidization of Si and B4C. Besides, the novel adhesive displayed good resistance to thermal-shock, especially for air-cooling test. After 15 thermal cycles in air, the residual strength of 1300 °C-calcined joints was still above 13 MPa (~40%).

materials science, ceramics